The pre-burying iron sheets approach was used to prepare rock-like materials with ordered multiple pre-cracks. 60 specimens in total were prepared in these experiments. Through biaxial compression experiments, the influence of both the number of pre-cracks and pre-cracks angles to crack growth was analyzed. Meanwhile, species of rock bridge failure were summarized, namely, wing crack, secondary shear crack between horizontal pre-cracks and secondary shear crack between vertical pre-cracks. The wing crack plays a significant role in crack growth. Furthermore, fractal dimension was adopted to describe quantitatively the crack growth during the failure process. The results indicate that with the failure of specimens, corresponding fractal dimension for specimen monotonically increases, which indicates that the fractal dimension can be considered to the failure of the specimens quantitatively.
英文摘要：
The pre-burying iron sheets approach was used to prepare rock-like materials with ordered multiple pre-cracks. 60 specimens in total were prepared in these experiments. Through biaxial compression experiments, the influence of both the number of pre-cracks and pre-cracks angles to crack growth was analyzed. Meanwhile, species of rock bridge failure were summarized, namely, wing crack, secondary shear crack between horizontal pre-cracks and secondary shear crack between vertical pre-cracks. The wing crack plays a significant role in crack growth. Furthermore, fractal dimension was adopted to describe quantitatively the crack growth during the failure process. The results indicate that with the failure of specimens, corresponding fractal dimension for specimen monotonically increases, which indicates that the fractal dimension can be considered to the failure of the specimens quantitatively.
同期刊论文项目
同项目期刊论文
Sequential Indentation Tests to Investigate theInfluence of Confining Stress on Rock Breakage by Tun
Numerical simulation on effects of embedded crack on rock fragmentation by a tunnel boring machine c
Mechanical Behavior of Brittle Rock-Like Specimenswith Pre-existing Fissures Under Uniaxial Loading:
期刊信息
位置：