中文摘要：

The study of controlled rolling/controlled cooling process parameters which affect the microstructure and mechanical properties of a novel pipeline steel has been optimized by the orthogonal experiment with four factors and three levels in this paper.However,the parameters of thermo-mechanical control process(TMCP)optimized by the Gleeble-3500 hot simulator could not satisfy performance requirements of the X100 pipeline steel.In order to improve the performance of this steel,the influence of finish cooling temperature(FCT) on the microstructure and property is studied in detail.It is found that,as this steel is thermo-mechanically treated by this set of parameters(the start heating temperature,finish rolling temperature(FRT),FCT and cooling rate of 1,180℃,810℃,350℃ and 35℃/s,respectively),the microstructures are mainly composed of granular bainite(GB)and acicular ferrite(AF).The effective grain sizes are below 20μm;the steel reaches the optimal balance between the strength and the toughness;the yield strength is 695 MPa;the tensile strength is 768 MPa;the elongation is 16.6%;the impact energy is 262 J at room temperature.All indexes could meet the requirements of X100 pipeline steel.

英文摘要：

The study of controlled rolling/controlled cooling process parameters which affect the microstructure and mechanical properties of a novel pipeline steel has been optimized by the orthogonal experiment with four factors and three levels in this paper. However, the parameters of thermo-mechanical control process （TMCP） optimized by the Gleeble-3500 hot simulator could not satisfy performance requirements of the X100 pipeline steel. In order to improve the performance of this steel, the influence of finish cooling temperature （FCT） on the microstructure and property is studied in detail. It is found that, as this steel is thermo-mechanically treated by this set of parameters （the start heating temperature, finish rolling temperature （FRT）, FCT and cooling rate of 1,180 ℃, 810 ℃, 350 ℃ and 35 ℃/s, respectively）, the micro- structures are mainly composed of granular bainite （GB） and acicular ferrite （AF）. The effective grain sizes are below 20 μm; the steel reaches the optimal balance between the strength and the toughness; the yield strength is 695 MPa; the tensile strength is 768 MPa; the elongation is 16.6 %; the impact energy is 262 J at room temperature. All indexes could meet the requirements of X100 pipeline steel.