中文摘要：

以中国白杨树无烟煤为原料,添加一定量煤焦油和沥青黏结剂制成炭棒作为阳极,采用直流电弧法制备竹节状碳纳米管及炭纳米纤维。用扫描电子显微镜（SEM）、透射电子显微镜（TEM）、能量散射谱（EDS）和X射线衍射（XRD）等技术对产物进行表征。结果表明：在较低氦气压力下（0.020M Pa）,采用不添加任何催化剂的无烟煤基炭棒进行电弧放电,在剩余阳极上制备得到竹节状碳纳米管和炭纳米纤维。所得竹节状碳纳米管多为开口状,直径在50nm左右;炭纳米纤维宏观上成绒毛球形,纤维的直径在30nm～50nm之间。

英文摘要：

Bamboo-like carbon nanotube （BCNTs） with open ends, and carbon nanofibers （CNFs） were prepared from a coal-based carbon rod by a DC arc discharge. The coal-based carbon rod was made by carbonizing Chinese Bai-Yang-Shu anthracite with coal tar and pitch as binder. The BCNTs and CNFs were characterized by scanning and transmission electron microscopy, energy dispersive spectroscopy, and X-ray diffraction. It is found that BCNTs and CNFs grow as a deposit on the anode at a low helium pressure of 0. 020 MPa with the coal-based carbon rod as anode. Most of the BCNTs have an open end and a diameter of 50 nm. CNFs with a diameter of 30-50 nm form fluffy balls on the surface of the remaining anode.