中文摘要：
对二维编织炭／炭复合材料（2D-C／C复合材料）进行压一压疲劳试验，疲劳加载条件分别为应力水平1000N、2000N和3000N，循环周次为10^4、1×10^5、3×10^5次时，并测试其疲劳加载前后试样的导热性能，研究了压-压疲劳加载对其导热性能的影响．结果表明，压-压疲劳加载没有改变2D-C／C复合材料试样的热扩散系数随温度升高而减小以及比热容随温度升高而增大的基本规律，但是压-压疲劳加载使其热导率、热扩散系数随着应力水平和循环周次的增大而降低，而其比热容的变化较小．在压-压疲劳加载过程中，2D-C／C复合材料疲劳损伤的产生和积累导致其导热性能降低．
英文摘要：
The compressive fatigue experiment of 2D-C/C composites was made under the stress level of 1000 N, 2000 N and 3000 N, cycling times of 104, 105 and 3× 105. the thermal conductivity behavior is tested before and after the fatigue loading, and the effects of compressive fatigue loading conditions on the thermal conductivity behavior of the composites were investigated. The results show that compressive fatigue loading does not change the law about the thermal diffusivity coefficient and specific heat capacity improve with the increasing temperature. However, after the compressive fatigue loading, the thermal conductivity coefficient, thermal diffusivity coefficient of the samples reduce with the increasing of the stress level and cycling times, while the specific heat capacity change little. The decline of the thermal conductivity is related to the fatigue damages generated and accumulated during the compressive fatigue loading after analysis.
同期刊论文项目
同项目期刊论文
Bamboo-shaped carbon nanofibers obtained in pyrolytic carbon by thermal gradient chemical vapor depo
Effect of Temperature on the Synthesis of SiC Coating on Carbon Fibers by the Reaction of SiO with t
High-temperature erosion resistance and aerodynamic oxidation mechanism of multi-layer MoSi2-CrSi2&n
Biotribology behavior of ultra-high molecular weight polyethylene against carbon/carbon composites u
Electrochemical performance of carbon nanotube-supported cobalt phthalocyanine and its nitrogen-rich
Oxidation protection of C/SiC coated carbon/carbon composites with Si-Mo coationg at high temperatur
B2O3 modified SiC-MoSi2 oxidation resistant coating for carbon/carbon by a two-step pack cementation
Modification of multi-walled carbon nanotubes with cobalt phthalocyanine: Effects of the templates o
Coefficients of thermal expansion of low texture and isotropic pyrocarbon deposited on stationary su
Density, microstructure and mechanical property of large-scale C/Ccomposites prepared by thermal gra
Electrophoretic deposition of carbon nanotubes onto carbon fiber felt for production of carbon/carbo
Effects of pre-deposited pyrocarbon on the microstructure and mechanical properties of carbon/carbon
Compressive properties of carbon/carbon composites reinforced by carbon nanotubes with different ori
Influence of heat treatment temperature on microstructure and thermal expansion properties of 2D car
期刊信息
位置：