中文摘要：
通过在Co82Zr18合金中添加过渡族元素Cr的方法,利用快淬工艺,制备出了Co82-xZr18Crx （x =0,2,3,4）快淬合金薄带.利用磁性测量、X光衍射、热磁分析、扫描电子显微镜,对其磁性能、相组成、微结构进行了研究.实验结果表明,在Co82Zr18合金中添加少量的Cr 可以使其矫顽力（iHc）显著提高.其中, Co79Zr18Cr3快淬薄带经600？C退火处理后iHc =6.5 kOe.相分析发现,600？C退火后的Co79Zr18Cr3快淬薄带由单一Co11Zr2相组成, Cr原子进入到了Co11Zr2相的晶格之中替换了原子半径相对较小的Co原子,这导致了Co11Zr2居里温度（TC）的降低却使其磁晶各向异性场（Ha）显著提高；另一方面,通过微结构研究发现,未退火的Co79Zr18Cr3快淬薄带由50-80 nm 的等轴晶粒组成.经600？C退火后,其晶粒形态并未发生改变然而晶粒尺寸却增长到400-500 nm.
英文摘要：
The Co82-xZr18Crx （x=0, 2, 3, 4） alloys are produced by melt-spinning. It is found that a proper addition of Cr can improve the coercivity significantly and a maximum coercivity of 6.5 kOe is obtained in the Co79Zr18Cr3 ribbon after having been annealed at 600 ？C. X-ray diffraction and thermomagnetic analysis are employed to determine its phase composition. It is found that the sample is comprised of the single Co11Zr2 and the Cr atoms enter into its lattice. A significant enhancement in the magnetocrystalline anisotropy field of Co11Zr2 is observed. SEM investigations show a microstructure consisting of equiaxed grains whose average size is about 400-500 nm. The coercivity enhancement in the Co79Zr18Cr3 alloy is ascribed to the increase in Ha.
同期刊论文项目
同项目期刊论文
Modeling of peptide-silica interaction based on four-body corrected fragment molecular orbital (FMO4
Effects of magnesium on phosphorus chemical states and p-type conduction behavior of phosphorus-dope
Electronic and optical properties of kesterite Cu 2 ZnSnS 4 under in-plane biaxial strains: First-pr
Preparation, characterization and mechanical properties of microarc oxidation coating formed on tita
Improvement of the coercivity of strontium hexaferrite induced by substitution of Al3+ ions for Fe3+
Effect of Nonmagnetic Impurity Doped on the Structural and Magnetic Properties of Quasi-one-dimensio
Brannerite-Type Vanadium-Molybdenum Oxide LiVMoO6 as a Promising Anode Material for Lithium-Ion Batt
Electrochemical properties and lithium-ion storage mechanism of LiCuVO4 as an intercalation anode ma
Synthesis and optimizable electrochemical performance of reduced graphene oxide wrapped mesoporous T
In situ Raman spectroscopy and X-ray diffraction of pressure-induced phase transition in columbite C
Synthesis of hollow alpha-Fe2O3-silica composites templated by poly(acrylic acid) colloidal aggregat
Synthesis of H2V3O8/Reduced Graphene Oxide Composite as a Promising Cathode Material for Lithium-Ion
Studies of the electrochemical properties and thermal stability of LiNi1/3Co1/3Mn1/3O2/LiFePO4 compo
Tunable valley polarization by a gate voltage when an electron tunnels through multiple line defects
First-principles study of 3d transition metal atom adsorption onto graphene: The role of the extende
Improvements in the electrochemical kinetic properties and rate capability of anatase titanium dioxi
Improved electrochemical performance of nitrogen doped TiO2-B nanowires as anode materials for Li-io
Na3V2(PO4)(3)/C composite as the intercalation-type anode material for sodium-ion batteries with sup
Studying of photoluminescence characteristics of CdTe/ZnS QDs manipulated by TiO2 inverse opal photo
Pre-resonance-stimulated Raman scattering for water bilayer structure on laser-induced plasma bubble
Hydrothermal synthesis and tunable luminescence of CaSiO3:RE3+(RE3+ = Eu3+, Sm3+, Tb3+, Dy3+) nanocr
Multi-pathway all-optical wavelength conversion switching and routing via four-and six-wave mixing i
Theoretical and Experimental Study of Photophysical Characteristics between Poly(9,9-dioctylfluorene
Effects of Nb s ubstitution for Zr on the structure and magnetic properties of Co80Zr18-xNbxB2 melt-
First-principles study of magnetic properties of stoichiometric and O deficient low-index surfaces o
Water soluble styrene butadiene rubber and sodium carboxyl methyl cellulose binder for ZnFe2O4 anode
Influence of laser-induced plasma on stimulated Raman scatting of OH stretching vibrational from wat
期刊信息
位置：