中文摘要：
在不同的焙烧温度下制备了Pt-Sn/SAPO-34催化剂,并使用X射线衍射、N2吸附、X射线荧光光谱、O2脉冲烧炭、H2程序升温还原和透射电镜等手段对催化剂进行了表征.在微型反应器中评价了Pt-Sn/SAPO-34催化剂对丙烷脱氢制丙烯反应的催化性能,考察了焙烧温度和反应气氛对催化剂性能的影响.结果表明,焙烧温度为500oC时,催化剂具有最佳的反应活性.当焙烧温度高于500oC时,催化剂出现不希望的表面变化,例如活性Pt位点的聚集、Pt的团聚、Sn的流失等.当反应温度为595oC时,Pt-Sn/SAPO-34催化性能稳定,且能够保持表面金属状态.
英文摘要：
Pt-Sn/SAPO-34 catalyst samples were prepared at different calcination temperatures.The catalysts were characterized by X-ray diffraction,N2 adsorption,X-ray fluorescence spectroscopy,O2-pulse coke content measurement,temperature-programmed reduction with hydrogen,and transmission electron microscopy.The activity was measured in a microreactor.The effect of calcination temperature and reaction atmosphere on the catalytic properties of Pt-Sn/SAPO-34 for propane dehydrogenation to propylene was investigated.The catalyst prepared at the calcination temperature of 500 oC showed the best performance,while the catalysts prepared above and below the 500 oC calcination temperature showed undesirable surface changes such as Pt active site degradation,Pt sintering,loss of Sn,etc.At the reaction temperature of 595 oC,Pt-Sn/SAPO-34 was stable and maintained surface metallic properties.
同期刊论文项目
同项目期刊论文
Pt-Sn-based catalyst';s intensification using Al(2)O(3)-SAPO-34 as a support for propane dehydrogena
Improvement of oil adsorption performance by a sponge-like natural vermiculite-carbon nanotube hybri
HEXENE CATALYTIC CRACKING OVER 30% SAPO-34 CATALYST FOR PROPYLENE MAXIMIZATION: INFLUENCE OF REACTIO
High selectivity production of propylene from n-butene: Thermodynamic and experimental study using a
Direct synthesis of a fluidizable SAPO-34 catalyst for a fluidized dimethyl ether-to-olefins process
In situ synthesis of SAPO-34 crystals grown onto alpha-Al2O3 sphere supports as the catalyst for the
Modulating the diameter of carbon nanotubes in array form via floating catalyst chemical vapor depos
Growth deceleration of vertically aligned carbon nanotube arrays: Catalyst deactivation or feedstock
The mass production of carbon nanotubes using a nano-agglomerate fluidized bed reactor: A multiscale
Synthesis of single-walled carbon nanotubes with narrow diameter distribution by calcination of a Mo
Synthesis of vertically aligned CNTs with hollow channel on Al2O3-Al substrate electroplated with fe
Synthesis of thin-walled carbon nanotubes from methane by changing the Ni/Mo ratio in a Ni/Mo/MgO ca
The confined growth of double-walled carbon nanotubes in porous catalysts by chemical vapor depositi
期刊信息
位置：