纳米晶Ni疲劳行为的实验研究

期刊名称：谢季佳，洪友士. 纳米晶Ni疲劳行为的实验研究.《金属学报》(2009), Vol.45, no.7
时间：0
分类：TG113.25[金属学及工艺—物理冶金;金属学及工艺—金属学]
作者机构：[1]中国科学院力学研究所非线性力学国家重点实验室,北京100190
相关基金：国家自然科学基金项目10772178和10721202以及非线性力学国家重点实验室青年基金资助感谢武晓雷研究员对论文提出的有益建议.
相关项目：材料强度及灾变的跨尺度力学研究

关键词：纳米晶Ni, 疲劳裂纹起源, 纳米硬度, 原子力显微镜, nanocrystalline Ni, fatigue crack initiation, nanoindentation, AFM

中文摘要：

系统研究了纳米晶Ni与粗晶Ni的疲劳行为．通过疲劳实验获得了这2种材料的疲劳应力一寿命衄线，并采用AFM对纳米晶Ni样品表面进行观察以研究其裂纹萌生的微观机制，利用纳米压痕仪对疲劳实验前后样品的力学性能和显微组织变化进行了研究．结果表明，纳米晶Ni具有比粗晶Ni更高的疲劳极限．AFM观察表明，纳米晶疲劳后样品表面出现平均尺寸为73nm的胞状起伏，疲劳后样品的晶粒尺寸未发生明显改变．压痕硬度结果表明，疲劳过程材料的力学性能也未发生明显变化．

英文摘要：

Electrodeposited nanocrystalline （nc） metal is often used as a model material in nc material investigation. But electrodeposition typically yields only thin foils that are at most several hundred micrometers in thickness, this arouses experimental difficulties in fatigue testing. There are several investigations on fatigue of electrodeposited nc metals. However, for the lack of direct experimental evidence, the mechanism of fatigue crack nucleation for nc materials is still not clear. In addition to fatigue properties, the microstructure stability is another key point for the practice of bulk nc materials. Some research papers indicated that the grains of nc metal would grow up under quasistatic loading, but no any investigation give out results under cyclic loading. In this paper, fatigue of electrodeposited nc Ni was experimentally investigated. Fatigue testing was carried out to obtain the S-N curves. For the reason that surface is the most important site for fatigue crack initiation, atomic force microscopy （AFM） was used to scan the sample surface before and after fatigue testing, which provides a direct observation on fatigue crack nucleation mechanism. For investigation on the stability of microstructure, the AFM was also used to measure the grain size of samples after fatigue loading, and nanoindenter was used to investigate the change of mechanical properties of samples after fatigue testing. The S-N curves indicate that nanocryatalline samples have a higher fatigue limit than coarse grain ones. The AFM images indicate that cell pellet morphology with the average size of 73 nm appeared on sample surface after high cycle fatigue testing and the grain size is the same as those before the fatigue testing. From the results of nanoindentation, the mechanical properties including hardness, strain rate sensitivity and elastic modules of samples also keep no obvious change after fatigue loading. Based on these results, the fatigue crack nucleation mechanism of electrodeposited nc Ni was discussed.