中文摘要：
以聚乙二醇（PEG）为改性剂，采用溶液燃烧法成功制备了准球形的PDP用BaMgAl10O17：Eu^2＋（BAM）蓝色荧光粉。通过X射线粉末衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）以及荧光光谱对获得的试样进行了表征。结晶表明，获得的BAM荧光粉颗粒为准球形、颗粒尺寸为20～40nm。当PEG的分子量（MW）为10000且质量百分比浓度为5．0％时，能获得最佳形貌和最高发光强度的BAM蓝色荧光粉。
英文摘要：
Starting from the aqueous solutions of metal nitrates with polyethylene glycol （PEG） as additives, the blue emitting BaMgAl10O17：Eu^2＋ （BAM） phosphor for PDP application was prepared by solution combustion method. X-ray powder diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and photoluminescence spectra were used to characterize the resulted BAM phosphor. The obtained BAM phosphor particles have spherical shape, nanometer size （20-40nm） and its average grain size is about 30nm. In this paper, the effect of PEG on the morphology and luminescence performance of the BAM phosphor was mainly investigated. The results show that adequate amount of PEG was necessary for obtaining spherical particles, and the optimum emission intensity was achieved when the concentration of PEG （ MW = 10000 ） was 5. 0wt% in the precursor solution.
同期刊论文项目
同项目期刊论文
Influence of sintering temperature on microstructures of Nb/Nb5Si3 in-situ composites synthesized by
Fabrication and microstructure evolution of niobium-niobium silicide composites by spark plasma sint
In-situ synthesis and characteristics of TiC-Fe cermet graded composite coating on a steel substrate
Microstructures, densification and mechanical properties of TiC–Al2O3–Al composite by field-activate
Influence of an electric field on combustion synthesis process and microstructures of TiC-Al2O3-Al c
The effect of citric acid to metal nitrates molar ratio on sol-gel combustion synthesis of nanocryst
Microstructures and densification of MoSi2-SiC composite by field-activated and pressure-assisted co
期刊信息
位置：