中文摘要：

采用热解处理已合成的聚吡咯纳米线实现一维碳纳米纤维的有效合成。在 KOH 的活化作用下，原始的纤维结构发生变化，获得带状碳纳米结构。对所合成的碳纳米线及碳纳米带进行形貌及结构表征。测试这两种一维碳纳米材料应于于锂离子电池中负极材料的电化学性能。结果表明，一维碳纳米线及一维碳纳米带均表现出较优的循环性能及良好的倍率性能。碳纳米线材料在循环50次后仍保持530 mA·h/g的可逆容量。在前23次充放电循环中，碳纳米带的可逆容量均高于850 mA·h/g，充放电循环到第23次的容量保持率为86%。

英文摘要：

An efficient synthesis of carbon nanofibers by pyrolysis of as-prepared polypyrrole nanowires was reported. Under the subsequent KOH activation, a significant morphology variation was detected and the obtained sample took on a ribbon-like structure. The morphology and structure of the carbon nanofibers and carbon nanoribbons were characterized. When the as-prepared one-dimensional carbon nanostructures were used as anode materials in lithium ion batteries, both of them exhibited superior cyclical stability and good rate properties. After 50 cycles, the reversible capacity of carbon nanofibers electrode maintained 530 mA·h/g. Concerning carbon nanoribbons, the reversible capacity is always larger than 850 mA·h/g and the reversible capacity retention after 23 cycles is 86%.