中文摘要：
利用激光熔化沉积工艺制备了TiB＋TiC增强相体积分数分别为9％、11％、22％及57％的4种（TiB＋TiC）／TAl5原位钛基复合材料。随增强相含量提高，TiB形态由片层状向棱柱状转化，TiC形态由不规则颗粒状向枝晶状转化，钛基复合材料硬度及弹性模量均显著提高而塑性明显下降。增强相体积分数约为9％的复合材料表现出较好的综合力学性能．增强相体积分数大于11％后复合材料的抗拉强度急剧降低。与激光熔化沉积态TAl5钛合金相比，TiB＋TiC增强相体积分数约为9％的复合材料抗拉强度（1040 MPa）及屈服强度（935MPa）均提高约12％。
英文摘要：
（TiB＋TiC）/TA15 in situ titanium matrix composites with 90%, 11%, 22% and 57% volume fractions of TiB＋TiC reinforcements, respectively were fabricated by the laser melting deposition manufacturing process. The morphology of TiB changes from plate like to prismatic while the morphology of TiC evolves from particle like to dendritic with the increasing volume fraction of the reinforcements. The Rockwell hardness and elastic modulus of the composites increase and the ductility decreases with the increasing volume fraction of TiB＋TiC reinforcements. The composite with a reinforcement volume fraction of 9% exhibits the optimum mechanical properties, while the tensile strength of the composites decreases abruptly when the reinforcement volume fraction is up to approximately 11%. The yield strength （935 MPa） and ultimate tensile strength （1040 MPa） of the laser melting deposited in situ （TiB＋TiC）/TA15 composite containing 9% volume fraction of TiB＋TiC reinforcements are both enhanced by 12% compared to the as-laser deposited titanium alloy TA15.
同期刊论文项目
同项目期刊论文
Microstructure and hot corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal s
Hot corrosion behaviors of a Cr13Ni5Si2-based metal silicide alloy in Na2SO4+25 wt.% K2SO4 and Na2SO
Microstructure and mechanical properties of rapid directionally solidified Ni-base superalloy Rene'4
High temperature mechanical properties of a laser melting deposited TiC/TA15 titanium matrix composi
Deformation Behavior in High-Frequency Fatigue Failure of Laser Melting Deposited Ti-6Al-2Zr-Mo-V Al
Microstructure and Tribological Property of Laser Melt Deposited alpha/Fe9Cr9Si2 Metal Silicide Allo
Effect of Annealing Temperatures on Microstructure and Mechanical Properties of Laser Melting Deposi
Microstructure and mechanical properties of directional rapidly solidified Ni-base superalloy Rene95
Microstructure and electrochemical characterization of laser melt-deposited Ti2Ni3Si/NiTi intermetal
Corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 multi-phase ternary metal silicide all
CORROSION BEHAVIORS OF Ni BASE SOLID SOLUTION-TOUGHENED Cr13Ni5Si2 ALLOY IN Cl- CONTAINING SOLUTIONS
Microstructure and dry sliding wear resistance of laser clad TiC reinforced Ti-Ni-Si intermetallic c
Microstructural characterization and dry sliding wear resistance of MoO2-strengthened gamma/NiMo all
Microstructure and tensile properties of laser melting deposited TiC/TA15 titanium matrix composites
Solidification microstructure and mechanical properties of corrosion-resistant ultrahigh strength st
Influence of Ni content on the microstructure and dry sliding wear properties of Cr13Ni5Si2/gamma in
Microstructure and wear resistance of laser melted Ti5Si3-TiCo-Ti2Co multiphase intermetallic alloys
期刊信息
位置：