中文摘要：
比较了未氧化处理与经浓硝酸或混酸（浓硫酸与浓硝酸体积比为1∶1）处理后的不同多壁碳纳米管（MWNTs）为载体的Pd催化剂（Pd/MWNTs）对水合肼氧化的电催化性能.光谱表征和电化学测试结果表明,MWNTs表面不修饰或修饰程度过大都不利于金属Pd纳米粒子的沉积.浓硝酸处理使MWNTs表面修饰的含氧基团适中,能够促进负载的Pd纳米粒子均一分布,因此提高Pd/MWNTs催化剂对水合肼的电催化性能.相反,混酸处理使MWNTs表面产生的含氧基团过多,导致金属Pd纳米粒子部分聚集,从而降低Pd/MWNTs催化剂对水合肼的电催化性能.
英文摘要：
Purified multi-walled carbon nanotubes（MWNTs） were treated with concentrated HNO3 or mixed acid [V（HNO3）∶V（H2SO4）=1∶1],respectively.When MWNTs were treated in concentrated HNO3 solution,suitable amount of hydrophilic O-containing surface groups would be formed.So the average size of the Pd nanoparticles deposited on the surface of the pretreated MWNTs is small and uniform,leading to the good electrocatalytic performance of the resulting Pd/MWNTs catalyst for the hydrazine electrooxida-tion.If purified MWNTs were untreated,the pristine surface of MWNTs prevented deposition of Pd nanoparticles on the surface of MWNTs,which lead to the aggregation of Pd nanoparticles.When MWNTs were treated in mix acid solution,the amount of the hydrophilic O-containing surface groups formed on MWNTs was abundant,which also resulted in the agglomeration of Pd nanoparticles.Consequently,the re-sulting Pd/MWNTs catalysts displayed the low electrocatalytic performance for the hydrazine electrooxida-tion.
同期刊论文项目
同项目期刊论文
Electrocatalytic oxidation and detection of hydrazine at carbon nanotube-supported palladium nanopar
Synthesis of carbon supported palladium nanoparticles catalyst using a facile homogeneous precipitat
Preparation of highly dispersed and ultrafine Pd/C catalyst and its electrocatalytic performance for
Highly dispersed carbon-supported Pd nanoparticles catalyst synthesized by novel precipitation-reduc
Ethanol electrooxidation on carbon-supported Pt nanoparticles catalyst prepared using complexing sel
Preparation of Pd-Au/C catalysts with different alloying degree and their electrocatalytic performan
Preparation of carbon supported Pd-P catalyst with high content of element phosphorus and its electr
Electro-catalytic performance of PdCo bimetallic hollow nano-spheres for the oxidation of formic aci
Electrochemical behavior of dopamine in the presence of phosphonate and the determination of dopamin
Effect of Pd ions in electrolyte on Electrocatalytic performance of carbon supported Pd catalyst foo
One-pot synthesis of three-dimensional platinum nanochain networks as stable and active electrocatal
Preparation of highly dispersed palladium-phosphorus nanoparticles and its electrocatalytic performa
A Novel Preparation of High Alloying PdFe/C Catalyst and Its Electrocatalytic Activity on the Oxygen
Electrostatic self-assembly of platinum nanochains on carbon nanotubes: A highly active electrocatal
Polyallylamine-directed green synthesis of platinum nanocubes. Shape and electronic effect codepende
Crystalline palladium-cobalt alloy nanoassemblies with enhanced activity and stability for the formi
One-Pot Water-Based Synthesis of Pt-Pd Alloy Nanoflowers and Their Superior Electrocatalytic Activit
Preparation of TiO2-Nanorods Supported Pd Catalyst and Its Electrocatalytic Oxidation on Formic Acid
Carbon supported Palladium-Iron nanoparticles with uniform alloy structure as methanol-tolerant elec
Improvement and mechanism of electrocatalytic performance 0f Pd-Ni/C anodic catalyst in direct formi
Room-temperature synthesis and electrocatalysis of carbon nanotutes supported palladium-iron alloy n
Probing the Interaction of Anti-Cancer Agent Dihydromyricetin with Human Serum Albumin: A typical Me
Surfactant-free palladium nanodendrite assemblies with enhanced electrocatalytic performance for for
Ferric ion immobilized on three-dimensional nanoporous gold films modified with self-assembled monol
位置：