中文摘要：

采用溶胶–凝胶法在700℃和较短的煅烧时间下制备了钙钛矿结构的CaZrO3和不同浓度的Eu3＋、Dy3＋掺杂的CaZrO3纳米晶粉末,对合成产物的发光性质进行研究。结果表明：Eu3＋掺杂的CaZrO3样品在590～630 nm之间有强的橙红光发射,在Eu3＋掺量为5.0%（摩尔分数,下同）时发光强度达到最高值。Dy3＋掺杂的CaZrO3样品分别在575 nm和485 nm处有强的黄光和蓝光发射,Dy3＋的最佳掺量为2.0%,此时浓度猝灭现象不明显。Eu3＋、Dy3＋共掺的CaZrO3样品表现为Eu3＋的发光,但其发光强度随着Dy3＋掺量的增大出现荧光猝灭现象

英文摘要：

The CaZrO3 nanocrystal with a perovskite structure and the CaZrO3 samples doped with different mole fraction of Eu3＋ and Dy3＋ were prepared by sol–gel method at 700 ℃ and under a short calcining time.The luminescent properties of products were inves-tigated.The results indicate that the Eu3＋-doped samples（Eu3＋：CaZrO3） exhibit strong orange-red light emission from 590 to 630 nm.Furthermore,the luminescent intensity of the Eu3＋：CaZrO3 sample doped with 5% in mole Eu3＋ reaches the maximum value.The Dy3＋-doped sample（Dy3＋：CaZrO3） shows strong yellow and blue light emissions in 575 nm and 485 nm respectively.The optimal doping quantity of Dy3＋ is 2.0% in mole and the concentration quenching of the 2.0%Dy3＋：CaZrO3 sample is not obvious.The CaZrO3 samples co-doped with Eu3＋,Dy3＋exhibit the same luminescent feature with the Eu3＋-doped sample,while the luminescence intensity of the sample occurs fluorescence quenching with the doping quantity of Dy3＋ increased.