中文摘要：

采用聚苯乙烯的N，N-二甲基甲酰胺溶液为原料，通过静电喷涂的方法制备了具有微．纳米复合结构的聚苯乙烯膜．通过调节溶液浓度，得到了不同的结构、浸润性及吸附性的表面．当聚苯乙烯的质量分数为5％、分子量为25000时，得到的表面与水的接触角达到167°，吸附力达到15μN，表明该膜表面具有超疏水性的同时对水滴具有很低的吸附力．此外，分子量的大小也对静电喷涂膜表面形貌的变化起重要的作用．

英文摘要：

Electro-spinning is widely accepted as a simple and versatile technique for producing micro- and nano-structures. Using this method, micro-nano structured polystyrene（ PS ） was prepaired by controlling the Concentration of PS/DMF solution. At 5% （mass fraction） PS/DMF solution with PS molecular weight of 250000, the surface shows super-hydrophobieity with water contact angle of about 167° and ultra-low adhesive force to water. Furthermore, molecular weight is also important to the surface morphology of the PS film formed by electro-spinning.