中文摘要：
采用提拉法成功生长了大尺寸高质量的 Ca4YO（BO3）3（YCOB）晶体，尺寸达到φ 110 × 90 mm3，为目前文献所报道的最大尺寸。有效的解决了YCOB 晶体生长过程中经常出现的开裂、螺旋生长等现象。在所生长的 YCOB 晶体基础上，加工了尺寸为 80 mm × 80 mm × 15 mm 的晶片用于进一步的实验。
英文摘要：
A large aperture and high quality Ca4YO（BO3）3 （YCOB） crystal was successfully grown using the Czochralski method. The dimension of the as-grown YCOB crystal was up to φ 110 × 90 mm3, which was the largest size to our knowledge. No cracks are ap- parent in the as-grown crystal. The crack and spiral growth can be effectively controlled in the as-grown crystalo The crystal plate with dimension of 80 mm × 80 mm × 15 mm was harvested from the as-grown crystal for further experiment.