中文摘要：

摘要研究了超声波（100W100kHz）对电沉积c0．Ni合金层的结构、形貌和性能的影响。结果表明：施加超声波可有效降低电沉积过程中浓差扩散的影响，促进阴极表面与镀液界面间的电子转移。超声波可降低Co-Ni合金层的Co含量并细化晶粒，使Co-Ni合金层更为平整。超声波影响Co-Ni合金层结构和形貌，可提高Co-Ni合金层的硬度以及在3．5％NaCl溶液中的耐腐蚀性。

英文摘要：

The effects of ultrasound agitation （100 W, 100 kHz） on the structure, morphology and prop- erties of electrodeposited Co-Ni alloy coatings were investigated in this paper. The result shows that： when ultrasonic agitation was used during the alloy coating electrodeposition, the concentration diffusion was effectively reduced, and the electron transfer between the cathode/solution interface was also pro- moted. Ultrasound agitation leads to the increase of Co content in alloy coating. The Co-Ni alloy coating deposited under ultrasound agitation is more fine-grained and uniform. The ultrasound agitation can lead to the enhancement of hardness and corrosion resistance properties of Co-Ni alloy coatings.