中文摘要：

采用坩埚下降法生长了尺寸为φ25mm×100mm的Ho^3＋掺杂的Bi4Si3O12（BSO：Ho）晶体，研究了所得晶体的透射光谱、激发光谱、发射光谱等特性。结果表明：BSO：Ho晶体透射光谱与纯BSO晶体基本一致，在350～800nm波长范围的透过率约为80％，吸收边在286nm处；在360、454和537nm处存在与Ho^3＋有关的吸收峰：激发光谱在240～310nm波段出现1个宽的激发带，峰值在290nm左右；发射光谱中除480nm发射带外，在573nm附近有多个与Ho^3＋有关的尖锐发射峰。BSO：Ho晶体的主要发光分量的荧光衰减时间为94．41ns，表明掺杂0．1％Ho^3＋（摩尔分数）有利于提高BSO晶体的闪烁性能。

英文摘要：

Ho-doped Bi4Si3O12 （BSO：Ho） crystal with 25 mm in diameter and 100 mm in length was grown by a modified vertical Bridgman method. The transmission spectra, excitation spectra, emission spectra and decay time of the as-grown crystal were investigated. Similar to pure BSO, BSO：Ho crystal has excellent optical transmittance. It is approximately 80% at 350-800 nm with an absorption edge at 286 nm, and some absorption peaks are related to Ho^3＋ doping appeared in the spectrum. The excitation band is located at 240-310 nm with the maximum peak at 290 nm. In addition to the emission band at 480 nm, there are several intense emission peaks at 573 nm, which are attributed to Ho^3＋ doping. The fluorescence decay time for main lighting component of BSO：Ho crystal is 94.41 ns, it indicate doping 0.1% Ho^3＋ （mole fraction） will help improve scintillation performance of BSO crystals.