中文摘要：

采用电弧喷涂技术在Q235钢基体上制备出纯锌、Zn-A1合金和zmAl伪合金涂层。通过浸泡试验和电化学测试考察涂层在3．5％NaCl溶液中的腐蚀行为，并结合扫描电镜（SEM）和X射线衍射仪（XRD）分析了涂层腐蚀后的表面形貌及腐蚀产物的相结构。结果表明，在3．5％NaCl溶液中三种涂层的耐腐蚀性按Zn_Al伪合金涂层、ZnA1合金涂层、Zn涂层的顺序依次降低。

英文摘要：

Pure Zn, Zn-A1 alloy and Zn-A1 pseudo-alloy coatings were prepared on Q235 steel surface by arc spraying technique. The corrosion resistance of these coatings was investigated by immersion testing and electrochemical measurements in 3.5%NaC1 solution. The surface morphology of the samples after test and the phase composition o{ corrosion products were analyzed by using electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the corrosion resistance of the coatings decreased sequentially in the order of Zn-AI pseudo alloy coating, Zn-A1 alloy coating, and pure Zn coating.