Sm2O3掺杂金属陶瓷惰性阳极的制备及性能研究
  • ISSN号:1000-4343
  • 期刊名称:《中国稀土学报》
  • 时间:0
  • 分类:TF111.522[冶金工程—冶金物理化学]
  • 作者机构:[1]东北大学材料与冶金学院,辽宁沈阳110004, [2]山东理工大学化学工程学院,山东淄博255049
  • 相关基金:国家自然科学基金(50374045)资助项目
中文摘要:

采用氧化铝-金属复合材料,适量掺杂稀土金属氧化物(Sm2O3),制备一种新型铝电解用氧化铝基金属陶瓷惰性阳极,并对添加稀土氧化物的材料综合性能进行了研究.结果表明: 添加稀土氧化物的试样晶粒生长完整,致密度高,耐高温和抗冰晶石熔盐腐蚀性能良好,年平均腐蚀速率为12.27 mm; 导电性能稳定、良好,其电导率随温度的升高而增大,具有半导体的导电性质,850 ℃时测得添加稀土氧化物的试样电导率为63 S·cm^-1.

英文摘要:

Cermets with adding rare earth oxide, used as inert anode in aluminum electrolysis, were prepared. The effect of rare earth oxide on properties of inert anode were researched. The results indicated that crystal of cermets with adding rare earth oxide growth ideally, the cermet inert anode had high density, high anti-oxidation, corrosion resistance and high conductivity. The annual corrosion rate of cermets with adding rare earth oxide was 12.27 mm/a. The conductivities increased with temperature increasing. The conductivities of cermets with adding rare earth oxide was 63 S·cm^-1 at 850 ℃.

同期刊论文项目
期刊论文 17 会议论文 3 获奖 2
同项目期刊论文
期刊信息
  • 《中国稀土学报》
  • 中国科技核心期刊
  • 主管单位:中国科学技术协会
  • 主办单位:中国稀土学会
  • 主编:徐光宪
  • 地址:北京新街口外大街2号
  • 邮编:100088
  • 邮箱:jrechina@263.net
  • 电话:010-62014832
  • 国际标准刊号:ISSN:1000-4343
  • 国内统一刊号:ISSN:11-2365/TG
  • 邮发代号:2-612
  • 获奖情况:
  • 优秀科技期刊奖,中国科协择优资助期刊,中国科协期刊奖
  • 国内外数据库收录:
  • 美国化学文摘(网络版),荷兰文摘与引文数据库,日本日本科学技术振兴机构数据库,中国中国科技核心期刊,中国北大核心期刊(2004版),中国北大核心期刊(2008版),中国北大核心期刊(2011版),中国北大核心期刊(2014版),中国北大核心期刊(2000版)
  • 被引量:12811