中文摘要：
在高温度梯度定向凝固炉中分别采用选晶法和籽晶法制备单晶高温合金,并采用XRD测定单晶的取向特征。结果表明,采用选晶法制备单晶高温合金时,在激冷板上随机形核的晶粒经过起晶段的竞争生长和螺旋段的选晶作用后,最终获得具有择优取向〈001〉的单晶。采用籽晶法制备单晶高温合金时,通过重熔籽晶的外延生长,所获得的单晶取向与籽晶取向保持一致。
英文摘要：
Single crystal superalloys have been prepared separately by a grain selector and a seeding technique in a high temperature gradient directional solidification furnace. The orientation characteristics were measured by XRD. Results indicate that for the grain selector method, the crystal solidification begins at the cooling plate with random nucleation, and through mutual competitive growth at the starter block. The grains enter the spiral selector, and finally the single crystal superalloys which are close to 〈001〉 direction are obtained. By the seeding technique, by epitaxial growth of partially melted seed crystals, single crystal superalloys which have the same orientation as the seed crystal are obtained.
同期刊论文项目
同项目期刊论文
Effect of Directional Solidification Methods onthe Cast Microstructure and Grain Orientation of Blad
Effect of carbon and boron additions on segregation behavior of directionally solidified nickel-base
Competitive grain growth mechanism in three dimensions during directional solidification of a nickel
Competitive grain growth mechanism in threedimensions during directional solidification of a nickel-
Influences of processing parameters onmicrostructure during investment casting of nickel-base single
The process analysis of seeding-grain selectionand its effect on stray grain and orientation control
期刊信息
位置：