中文摘要：

将紫外光照射条件下亚甲基蓝功能化的多壁碳纳米管（f1-MWCNTs）作为 Au 纳米粒子的载体, Au纳米粒子通过光化学还原法制备获得后,负载于f1-MWCNTs表面。傅立叶变换红外吸收光谱（FT-IR）表明,f1-MWCNTs 表面存在 C-N 基团和 N-H基团,为Au 纳米粒子的负载提供了活性位点。透射电镜（TEM）和X射线衍射谱（XRD）表明,Au 纳米粒子粒径约4.5 nm 左右,具有面心立方晶体结构,Au纳米粒子在f1-MWCNTs表面分散性良好。电化学实验结果表明,光照条件下改性碳纳米管所制备的催化剂（Au/f1-MWCNTs）对甲醇具有优异的催化性能,其质量电流密度是未经光照改性的碳纳米管负载 Au 纳米粒子催化剂（Au/f0-MWCNTs）的1.56倍。

英文摘要：

In this paper,functionalized MWCNTs were used as a new support for Au nanoparticles synthesized by photochemical reduction.MWCNTs were modified by methylene blue under ultraviolet light （f1-MWC-NTs）,and then Au nanoparticles were assembled on the surface of f1-MWCNTs.Fourier transform infrared （FT-IR）absorption spectroscopy revealed that C-N group and N-H group existed in the surface of f1-MWC-NTs.These groups might be active sites for Au nanoparticles loaded on the f1-MWCNTs.The morphology and structure of catalysts were characterized by transmission electron microscopy （TEM）and X-ray diffraction spec-trum （XRD）.The consequences showed that Au nanoparticles with face-centered cubic crystal structure were about 4.5 nm in size,and were uniformly dispersed on the surface of f1-MWCNTs.Electrochemical experi-ments indicated that the Au/f1-MWCNTs catalyst exhibited excellent catalytic performance for methanol oxida-tion in alkaline solution,and the mass specific current density of the peak for Pd/f1-MWCNTs was 1 .5 6 times higher than that of Au/f0-MWCNTs,which were functionalized by methylene blue without ultraviolet irradia-tion.