中文摘要：
采用电泳沉积法在Pt／Ti／SiO2／Si基底上制备了厚度为33μm的Ba0．6Sr0．4TiO3（BST40）厚膜，研究了其介电调谐特性、漏电流特性和铁电特性．实验结果表明：采用水热法制备纳米BST40粒子，经250MPa高压压制，950℃热处理后，BST40厚膜可形成完整的立方钙钛矿结构且表面致密、无裂纹．ε—V特性表明，1kHz时厚膜调谐率可达59．2％．I-V特性表明，当电压从-25～25V变化时，漏导电流〈100μA／cm^2．测量了在1kHz，不同温度下厚膜的电滞回线．在0℃时，其剩余极化强度为1．06μC／cm^2．
英文摘要：
Ba0.6Sr0.4TiO3 （BST40） thick film with thickness of 33μm was prepared by electrophoretic deposition method on Pt/Ti/SiO2/Si substrate using the BST40 nano powders as precursor. A high pressure treatment process was introduced in order to increase the density and decrease the sintering temperature of the film. The composition and surface morphology of the BST40 thick film were characterized. The ε-V curve of the BST40 thick film was measured. The leakage current density was tested and hysteresis loops of the thick film were measured at different temperatures. The results show that a dense and no crack surface are formed after sintering at 950℃. A tunability of 59.2% is calculated according to the ε-V curve. The leakage current is less than 100μA/cm^2 when the applied voltage shifts from 25V to 25V. The remnant polarization is 1.06μC/cm^2 at the temperature of 0℃ and the frequency of 1kHz.
同期刊论文项目
同项目期刊论文
Electromagnetic Transmission Property in Split-Ring Resonators at Microwave Frequency by Finite Diff
Polaron relaxation associated with the localized oxygen vacancies in Ba0.85Sr0.15TiO3 ceramics at hi
Oxygen vacancy-induced aging of Mn-doped Ba0.8Sr0.2TiO3 ceramics in paraelectric and ferroelectric s
Effects of Na/K evaporation on electrical properties and intrinsic defects in Na0.5K0.5NbO3 ceramics
Electrostatic spray deposited polycrystalline zinc oxide films for ultraviolet luminescence device a
Relaxor behavior and dielectric properties of lead magnesium niobate-lead titanate thick films prepa
Synthesis and formation mechanisms of high aspect ratio platelike NaNbO3 particles by topochemical m
Bi3.25La0.75Ti3O12 powders by the complex polymerization method: synthesis, characterization and mor
Optimizing design of the microstructure of sol-gel derived BaTiO 3 ceramics by artificial neural net
Low-temperature fabrication and crystallization behavior of Pb(Mg1/3Nb2/3O3) crystallites by a hydro
Electrical properties and microstructural characteristics of nonstoichiometric CaCu3xTi4O12 ceramics
Microstructure and dielectric properties of La2O3 films prepared by ion beam assistant electron-beam
Anomalous phase formation during annealing of La2O3 thin films deposited by ion beam assisted electr
The dielectric properties and the relaxation phase transition of copper substituted SrBi2Nb2O9 ferro
Optical and electrical properties of La2O3 films prepared by ion beam assistant electron beam evapor
Effect of sintering temperature on the structure and properties of cerium-doped 0.94(Bi0.5Na0.5)TiO3
Lorentz-type relationship of the temperature dependent dielectric permittivity in ferroelectrics wit
Effects of depositing temperatures on structure and optical properties of TiO2 film deposited by ion
Preparation and electrical properties of BST thick film deposited by electrophoretic deposition meth
Structural and electric properties of barium strontium titanate based ceramic composite as a humidit
Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite s
Preparation and characterization of perovskite Pb(Mg1/3Nb 2/3)O3-PbTiO3 by a modified polymerized co
Microstructure and electrical properties of the rare-earth doped 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 piezo
Dielectric, ferroelectric properties, and grain growth of CaxBa1-xNb2O6 ceramics with tungsten-bronz
Structure and electric properties of poly(vinylidene fluoride-tetrafluoroethylene) copolymer studied
Structure, phase transition and electric properties of poly(vinylidene fluoride-trifluoroethylene) c
Epitaxial growth and electrical characterization of PBZT thin films by RF magnetron sputtering depos
Modeling the Al2O3 particle-polymer composites for the packaging of the shock-wave pulsed transducer
期刊信息
位置：