中文摘要：
以2-丙烯酰胺基-2-甲基丙磺酸（AMPS）作引发剂引发交联聚乙烯醇（PVA）-戊二醛（GA）制备水凝胶聚合物电解质并组装成超级电容器.分别由红外光谱、交流阻抗、循环伏安与恒电流充放电测定该凝胶聚合物电解质及超级电容器的电化学性能.结果表明,该聚合物电解质电导率可达1.23 mS/cm（室温）.而且,以1.0 gAMPS引发0.05 mL GA（5%）与1.0 g PVA交联,制得的凝胶聚合物电解质超级电容器比电容可达139 F/g,50次充放电后其值仍在80%以上.
英文摘要：
The supercapacitor based on the hydrogel polymer electrolyte prepared by the cross-linking polyvinyl alcohol-glutaraldehyde（PVA-GA） using 2-acrylamido-2-methyl propane sulfonic acid（AMPS） as an initiator were assembled.The electrochemical properties of the gel polymer electrolytes and supercapacitors were studied by FTIR,AC impedance,cyclic voltammetry and constant current charge-discharge measurements.The results showed that the ionic conductivity of the ploymer electrolyte reached 1.23 mS/cm at room temperature.The specific capacitances were 139 F/g with AMPS of 1.0 g to 0.05 mL of 5%（by mass） GA cross-linking with 1.0 g PVA.And the specific capacitances retained above 80% after 50 cycles of charge-discharge.
同期刊论文项目
同项目期刊论文
Application of Thermosetting Organic Solvent Free Polymer Gel Electrolyte in Quasi-Solid-State Dye-S
Application of poly(acrylic acid-g-gelatin)/polypyrrole gel electrolyte in flexible quasi-solid-stat
The preparation of poly(glycidyl acrylate)-polypyrrole gel-electrolyte and its application in dye-se
Low cost poly(3,4-ethylenedioxythiophene):polystyrenesulfonate/carbon black counter electrode for dy
Preparation of PAA-g-CTAB/PANI polymer based gel-electrolyte and the application in quasi-solid-stat
Enhancing photovoltaic performance of dye-sensitized solar cell by rare-earth doped oxide of Lu2O3:(
Quasi-solid-state dye-sensitized solar cell based on a polymer gel electrolyte with in situ synthesi
Preparation of sub-micron size anatase TiO2 particles for use as light-scattering centers in dye-sen
Enhancing photoelectrical performance of dye-sensitized solar cell by doping with europium-doped ytt
Dye-sensitized solar cell with a solid state organic-inorganic composite electrolyte containing cata
Quasi-solid- state dye-sensitized solar cells containing P (MMA-co-AN)-based polymeric gel electroly
Application of Poly(3,4-ethylenedioxythiophene):Polystyrenesulfonate/Polypyrrole Counter Electrode f
Bi-functional TiO2 cemented Ag grid under layer for enhancing the photovoltaic performance of a larg
Preparation of poly(acrylic acid)/gelatin/polyaniline gel-electrolyte and its application in quasi-s
Preparation of Single-Crystalline TiO2 Nanowires and Their Application in Flexible Dye-Sensitized So
Controllable hydrothermal synthesis of nanocrystal TiO2 particles and their use in dye-sensitized so
Preparation of hierarchical tin oxide microspheres and their application in dye-sensitized solar cel
Facile Synthesis of Mesoporous Tin Oxide Spheres and Their Applications in Dye-Sensitized Solar Cell
Low temperature fabrication of high performance and transparent Pt counter electrodes for use in fle
Enhancement of the Photovoltaic Performance of Dye-Sensitized Solar Cells by Doping Y0.78Yb0.20Er0.0
A Large-Area Light-Weight Dye-Sensitized Solar Cell based on All Titanium Substrates with an Efficie
Glucose Aided Preparation of Tungsten Sulfide/Multi-Wall Carbon Nanotube Hybrid and Use as Counter E
期刊信息
位置：