中文摘要：
采用溶胶凝胶法制备了碳载纳米双金属Ni-Pt（5%,质量分数）/C电催化剂,用TEM、XRD和XPS表征金属粒子的形貌、晶相结构、表面元素及其价态,循环伏安法测试催化剂在碱性溶液中电催化氧化甲醇的活性。结果表明,Ni-Pt金属粒子在碳载体上分布均匀,粒径为3～6nm,少量Pt的掺杂对纳米Ni活性有明显提高,其中,合金型Ni-Pt（5%）/C在1.0mol/LNaOH＋1.0mol/LCH3OH溶液中峰电流密度可达85.6mA/mg,是Ni/C峰电流密度的8.7倍,达到Pt/C峰电流密度的15.3%。单位质量铂的电流显著提高。
英文摘要：
Carbon supported nano-nickel-platinum electrocatalyst samples of Ni-Pt（5wt%）/C were prepared by the colloidal-gelatin method.Transmission electron microscopy（TEM）,X-ray diffraction（XRD） and X-ray photoelectron spectroscopy（XPS） were used to evaluate the metal particles＇ morphology,crystal configuration,superficial element constitution and value.Moreover,cyclic voltammeter was employed to measure the catalytic activity for the electro-catalytic oxidation of methanol in an alkaline medium.The results show that Ni-Pt particles are distributed homogeneously on the carbon,with the particle sizes of 3-6 nm;the Pt doping improves largely the activity of Ni nano-particles,and the peak current density of alloy Ni-Pt（5wt%）/C catalyst reaches 85.6 mA/mg in the solution of 1.0 mol/L NaOH ＋ 1.0 mol/L CH3OH,which is 8.7 times of that of Ni/C,and 15.3% of that of Pt/C.The current of Pt per unit mass is increased obviously.
同期刊论文项目
同项目期刊论文
期刊信息
位置：