中文摘要：
主要研究了钒钛基脱硝催化剂失活机理及再生。采用SEM、EDS、XRD、BET等手段对国内某家燃煤火电厂运行20000h的SCR脱硝催化剂进行表征,然后使用0.5mol/L的硫酸和0.01mol/L的氢氟酸对运行过的催化剂进行了清洗再生并通过烟气模拟-催化剂活性测试系统考察了催化剂的脱硝活性。结果表明,相比于新鲜催化剂,运行后的催化剂活性明显下降,孔容和比表面积有所下降,其表面存在着组成复杂的飞灰,飞灰主要成分为SiO2;采用0.01mol/L氢氟酸溶液清洗能够明显恢复催化剂的脱硝活性,这是因为氢氟酸可以有效清除失活催化剂表面的SiO2。
英文摘要：
Deactivation and regeneration of V2O5/TiO2 catalyst for elimination of NO were studied, lhe spent V2O5/TiO2 catalyst sample was from a domestic power plant, which had been operated for 20000h. The spent V2O5/TiO2 catalyst was characterized by SEM, EDS, XRD and BET techniques to reveal the deactivation mechanism. The regeneration of V2 O5/TiO2 catalyst was conducted by washing with aqueous solution of 0.5 mol/L H2SO4 or 0.01mol/L HF. The results showed that the actvity of the spent catalyst dropped greatly in comparison with the fresh catalyst. The reason was that the spent catalyst was heavily covered by ash which blocked the active sites and plugged the pores. After the spent catalyst was washed with aqueous solutions of 0.01mol/L HF, the activity of regenerated catalyst was improved significantly due to effective removal of sili- con dioxide covered on the spent catalyst, a main composition of the ash.
同期刊论文项目
同项目期刊论文
Dynamics and Isotherms of Water Vapor Sorption on Mesoporous Silica Gels Modified by Different Salts
Effect of gasoline composition on oxidative desulfurization using a phosphotungstic acid/activated c
Adsorption Isotherms, Kinetics, and Desorption of 1,2-Dichloroethane on Chromium-Based Metal Organic
?From Alkyl Aromatics to Aromatic Esters: Efficient and Selective C-H Activation Promoted by a Bimet
Metal-Organic Framework Supported Gold Nanoparticles as a Highly Active Heterogeneous Catalyst for A
A microporous, moisture-stable, and amine-functionalized metal-organic framework for highly selectiv
Oxygen permeation through a CO2-tolerant mixed conducting oxide (Pr0.9La0.1)(2)(Ni0.74Cu0.21Ga0.05)O
Multifunctional Catalysis by Pd@MIL-101: One-Step Synthesis of Methyl Isobutyl Ketone over Palladium
Hierarchically structured Beta zeolites with intercrystal mesopores and the improved catalytic prope
Synthesis and structural properties of hierarchically structured aluminosilicates with zeolite Y (FA
Mesoscopic simulation of surfactant/silicate self-assembly in the mesophase formation of SBA-15 unde
Carbon nanotube catalysts for oxidative desulfurization of a model diesel fuel using molecular oxyge
Equilibrium and Do-Do Model Fitting of Water Adsorption on Four Commercial Activated Carbons with Di
Synthesis and adsorption performance of MIL-101(Cr)/graphite oxide composites with high capacities o
Decomposition of Toluene in a Plasma Catalysis System with NiO, MnO2, CeO2, Fe2O3, and CuO Catalysts
Adsorption of Dibenzothiophene on Ag/Cu/Fe-Supported Activated Carbons Prepared by Ultrasonic-Assist
Effects of Metal Ions and Ligand Functionalization on Hydrogen Storage in Metal-Organic Frameworks b
Effect of Textural Properties on the Adsorption and Desorption of Toluene on the Metal-Organic Frame
Adsorption and Diffusion of Benzene on Chromium-Based Metal Organic Framework MIL-101 Synthesized by
In situ 2,5-pyrazinedicarboxylate and oxalate ligands synthesis leading to a microporous europium&nd
期刊信息
位置：