中文摘要：

以钛酸四丁酯为钛源、十八水硫酸铝为铝源、三乙醇胺为模板剂，采用研磨一溶胶技术合成了A1掺杂的Ti02介孔材料，并利用XRD、EDS、TEM、BET、UV-vis和IR等手段表征了材料的结构、形貌、比表面积、孔径分布及光学性能。结果表明：Al掺杂能够减小Ti02光催化剂的粒径，提高介孔TiO2的热稳定性；Al掺杂TiO2介孔材料的平均孔径为4．5nm，比表面积达到110．2m2／g；相比商用P25和介孔Ti02，A1掺杂介孔Ti02的吸收边发牛红移，对初始浓度为20mg／L的甲基橙进行催化降解1h后，其降解率达到92．5％。

英文摘要：

Abstract： Using tetrabutyl orthotitanate （TBOT） as Ti source, Al2（SO4）2· 18H20 as A1 source and triethanolamine as atemplate, Al-doped TiO2 mesoporous materials were synthesized via grinding-sol-gel method. The structure, morphology, crystalline size, specific surface area, pore size and photocatalytic activity of the as-prepared samples were characterized by X-ray diffractometry, high-resolution transmission electron microscopy （HRTEM）, N2 adsorption desorption and UV-vis spectrometer （UV-vis） techniques. The results show that Al-doped TiO2 has the wormhole-like mesoporous structure, and the A1 doping can not only decrease the particle size of nanoparticles, but also improve the stability of the mesoporous TiO2. The specific surface areas and the average pore diameter ofAl-doped TiO2 is about 110.2 m2/g and 4.5 nm, respectively. Compared with P25 and mesoporous TiO2, the gap adsorption edge of Al-doped TiO2 mesoporous materials exhibit a little red shift, the degradation ratio of which can be up to 92.5% during the photodegradation of methyl orange with the initial concentration of 20 mg/L for 1 h.