采用溶胶-凝胶法制备了TiO2/Ti电极,X射线衍射（XRD）分析表明,TiO2主要为锐钛矿,晶粒尺寸约为46nm。以TiO2/Ti电极作阳极,Cu电极作阴极,组装成转盘液膜反应器,考察了其光电催化处理染料罗丹明B（RhB）的影响因素（转盘转速、偏压、溶液初始pH、RhB初始浓度和电解质浓度）。得到最佳处理条件为：转盘转速90r/min,偏压0.4V,溶液初始pH 2.5,电解质（硫酸钠）质量浓度0.5g/L。在最佳处理条件下,处理20mg/L RhB染料废水90min的脱色率和总有机碳（TOC）去除率分别达到97.2%和72.7%。结果表明,由于同时强化了激发光源的利用率和溶液的传质效率,TiO2/Ti转盘液膜反应器可高效光电催化处理染料废水。
英文摘要：
TiO2/Ti electrode was prepared by sol-gel method for photoelectrocatalysis treatment of the Rhodamine B（RhB） solution in a rotating disk thin-film reactor.X-ray diffraction（XRD） analysis showed the TiO2 photocatast was anatase with grain size of 46 nm.The effect of rotating speed,bias potential,initial pH,initial RhB concentration and supporting salt concentration on RhB degradation was investigated and the optimal treatment conditions were obtained as follow：rotating speed 90 r/min,bias potential 0.4 V,initial pH 2.5 and supporting salt concentration 0.5 g/L.Under these conditions,color and TOC removal efficiency of 20 mg/L RhB solution reached 97.2% and 72.7% respectively after 90 min treatment.The perfect performance of TiO2/Ti rotating disk thin-film reactor for RhB degradation could be attribute to its enhancement to light utilization efficiency and mass transfer velocity.
同期刊论文项目
同项目期刊论文
Decolorization of Rhodamine B in a thin-film photoelectrocatalytic (PEC) reactor with slant-placed T
Solvothermal Synthesis of Flower-like BiOBr Microspheres with Highly Visible-Light Photocatalytic Pe
Photocatalytic Fuel Cell (PFC) and Dye Self-Photosensitization Photocatalytic Fuel Cell (DSPFC) with
Aerosol-spraying preparation of a mesoporous hollow spherical BiFeO3 visible photocatalyst with enha
Ionic-liquid-assisted growth of flower-like TiO2 film on Ti substrate with high photocatalytic activ
Citric acid assisted solvothermal synthesis of BiFeO3 microspheres wit high visible0light photocatal
Effect of inorganic anions on Rhodamine B removal under visible light irradiation using Bi2O3/Ti rot
Condition optimization of amperometric determination of chemical oxygen demand using boron-doped dia
Highly active and stable CdS-TiO2 visible photocatalyst prepared by in-situ sulfurization under supe
Aerosol-spraying preparation of Bi2MoO6: A visible photocatalyst in hollow microspheres with a porou
Preparation of Mn2O3/SBA-15 catalyst with high loading and catalytic peroxidation for degradation of
Preparation and visible light catalytic activity of three-dimensional ordered macroporous CdS/TiO2 f
A high-efficient rotating disk photoelectrocatalytic (PEC) reactor with macro light harvesting pyram
Ordered macroporous Bi2O3/TO2 film coated on a rotating disk with enhance photocatalytic activity un
Dual slant-placed electrodes thin-film photocatalytic reactor: Enhanced dye degradation efficiency b
期刊信息
位置：