中文摘要：
为研究爆炸荷载作用下高强钢筋混凝土梁的抗弯性能,对不同钢筋强度的钢筋混凝土简支梁进行了爆炸试验,从构件的破坏形态、受力和变形特征分析了高强钢筋对试验简支梁抗弯性能的影响.结果表明：高强钢筋强度高的优势在爆炸荷载超过普通RC梁的屈服荷载后才能充分发挥.爆炸荷载较大时,裂缝数量较多的高强RC梁比普通RC梁具有更好的变形恢复能力,损伤程度显著减小.采用高强钢筋使得RC梁裂缝分布区域增大,在塑性变形阶段形成了梁长约60%的塑性区域,改变了RC梁塑性变形阶段的振型.
英文摘要：
In order to research the flexural behavior of concrete beams with high-strength reinforcements under blast loading,explosion tests on simply supported reinforced concrete beams with different reinforcement strength were conducted.Based on the failure pattern,stress and deformation characteristics of the beams,analysis of the influence caused by high-strength reinforcements on flexural behavior were made.It is showed that the strength advantages of high strength reinforcements can be fully functioned under blast loading which exceeds the yield load of the ordinary RC beams.When the blast loading is rather large,compared with the ordinary RC beams,the high-strength RC beams with more cracks have better deflection restoring capacity and a small degree of damage.The high-strength reinforcements adopted in RC beams result in a large crack distribution area,which is approximately as long as 60% of the beam span during the stage of plastic deformation and can change the vibration mode of RC beams during the plastic deformation stage.
同期刊论文项目
同项目期刊论文
A New Elasto-Viscoplastic Damage Model Combined with the Generalized Hoek-Brown Failure Criterion fo
Non-euclidean continuum model of the zonal disintegration of surrounding rocks around a deep circula
Experimental study on the Crack Initial Stress and the Crack Damage Stress of Red Sandstone Under Di
Dynamic Analysis for Collision Between a Plate and Supports Subjected to Instantaneous Protection St
A numerical method to determine the steady state distribution of passive contaminant in generic vent
Experimental Study on PC Beams Dynamic Performance of Prestress Degree under the Plane Charge Loadin
Effects of the axial in situ stresses on the zonal disintegration phenomenon in the surrounding rock
Dynamic responses of buried arch structure subjected to subsurface localized impulsive loading: Expe
Dynamic anti-crushing behaviors of woven textile sandwich composites: multilayer and gradient effect
Experimental Study on the Impermeability of Concrete Construction Joints with Different Geometric Sh
Zonal disintegration mechanism of cross-anisotropic rock mass around a deep circular tunnel under dy
Elastic responses of underground circular arches considering dynamic soil-structure interaction: A t
Failure mechanisms of sandwich composites with orthotropic integrated woven corrugated cores: Experi
A new elasto-viscoplastic damage model combing with generalized Hoek-Brown failure criterion for the
The non-Euclidean model of failure of the deep rock masses under the deformation incompatibilty cond
3D numerical modelling of projectile penetration into rock-rubble overlays accounting for random dis
Three-dimensional modelling of steel fiber reinforced concrete material under intense dynamic loadin
Quantitative analysis of potential rockburst of microcrack-weakened Surrounding rock mass in deep tu
Different crack sizes analyzed for surrounding rock mass around underground caverns in Jinping I hyd
期刊信息
位置：