通过酸碱处理与机械处理相结合的方法从木粉中提取出高长径比纳米纤维素，再利用真空过滤的方法制备高强度透明纳米纤维素膜。纳米纤维素的直径主要分布在30～100nm之间，纳米纤维素膜的拉伸强度高达101．79MPa，弹性模量高达5741MPa，透过率高达86．9％。
英文摘要：
A method used mechanochemical treatment to obtain cellulose from poplar. The high strength transparent nano cellulose film was further processed by vacuum filter. The cellulose was mainly range between 30-100 nm, tensile strength was reached up to 101.79 MPa, and elastic modulus was reached up to 5 741 MPa and the transparency reached up to 86.9%.
同期刊论文项目
同项目期刊论文
Strong and optically transparent biocomposites reinforced with cellulose nanofibers isolated from pe
Three kinds of charcoal powder reinforced ultra-high molecular weight polyethylene composites with e
Foldable and free-standing 3D network electrodes based on cellulose nanofibers, carbon nanotubes and
Optical and flexible α-chitin nanofibers reinforced poly(vinyl alcohol) (PVA) composite film: Fabric
High-performance nanocomposite films: reinforced with chitosan nanofiber extracted from prawn shells
The dynamical viscoelasticity and tensile property of new highly filled charcoal powder/ultra-high m
Dissolution and gelation of alpha-chitin nanofibers using a simple NaOH treatment at low temperature
Carbon fiber reinforced highly filled charcoal powder/ultra high molecular weight polyethylene compo
Preparation of Ultralong Cellulose Nanofibers and Optically Transparent Nanopapers Derived from Wast
Flexible highly specific capacitance aerogel electrodes based on cellulose nanofibers, carbon nanotu
A three-dimensionally chitin nanofiber/carbon nanotube hydrogel network for foldable conductive pape
Properties of polymethyl methacrylate-based nanocomposites: Reinforced with ultra-long chitin nanofi
Preparation and Properties of Optically Transparent Chitin Nanofibers Sheet by Different Simple Mech
期刊信息
位置：