以Li2CO3和Ni—Co—Mn三元系氧化物为原料，在空气中通过固相反应制备LiNi0．45Co0．10Mn0．45O2。研究反应条件对产物结构的影响，采用扫描电镜（SEM）表征样品的形貌，用粒度分析、振实密度和比表面测定等手段比较不同合成条件对产物性能的影响。研究结果表明：当n（Li）／n（M）不同时合成的产物性能差别很大，较适宜的n（Li）／n（M）为1．4／1：球磨可以提高产物的振实密度和比表面，并且对改善材料电化学性能有显著影响，在2．75-4．25V电压范围内LiNi0．45Co0．10Mn0．45O2首次放电比容量达到125．9mA·h／g，50次循环后放电比容量为128．7mA·h／g。

英文摘要：

LiNi0.45Co0.10Mn0.45O2 was prepared by solid-state reaction method in air using Li2CO3 and Ni-Co-Mn as starting materials. The effect of reaction conditions on the structure of the product was studied. The morphology of LiNi0.45Co0.10Mn0.45O2 was characterized by scanning electron microscopy. The effect of preparation conditions on the performance of the product was characterized by particle analyzer, tap-density and specific surface area. The results show that the mole ratio of Li to M has a critical role in the performance of the product and the suitable mole ratio of Li to M is about 1.4/1. Ball-milling is a useful method to improve the performances such as tap-density, specific surface area and has significant effects on the electrochemical performance. In the voltage ranges of 2.75-4.25 V, the initial discharge capacity of LiNi0.45Co0.10Mn0.45O2 is 125.9 mA·h/g, and the discharge capacity is 128.7 mA·h/g after 50 cycles.