中文摘要：
采用恒电位临界点蚀温度（CPT）法,利用OM,SEM,EDX和恒电位极化技术等研究了等离子弧焊接对双相不锈钢UNSS32304焊接接头微观组织及其耐点蚀性能的影响.结果表明,焊接接头热影响区和熔合区微观组织较母材相比发生了显著变化,两相比例严重失衡,铁素体所占比例均大于70%;两区域微观组织形态发生明显变化.且在铁素体晶粒内及两相相界处析出大量氮化物;焊接接头的耐点蚀性能明显下降,点蚀优先发生在高温热影响区所在的铁素体晶粒内.
英文摘要：
Microstructure and pitting corrosion resistance of UNS S32304 duplex stainless steels welded joint with plasma-arc welding（PAW） were studied by means of OM.SEM,energy dispersive X ray spectroscopy（EDX） and potentiostatic electrochemical technique.The results show that the microstructures of the heat-affected zone（HAZ） and fusion zone differ from the base metal greatly, with ferrite fraction greater than 70%.Furthermore,a lot of nitrides are precipitated at the interface between ferrite and austenite phases and inside the ferrite grains.Consequently,pitting corrosion resistance of the welded joint declines obviously and pitting preferentially occurs at ferrite phase in the high temperature HAZ near the fusion line.
同期刊论文项目
同项目期刊论文
Cerium chemical conversion coatings for corrosion protection of stainless steels in hot seawater env
Effect of SO2 on oxidation of type 409 stainless steel and its implication on condensate corrosion i
Pitting Resistance of Anodic Passive Films Formed on 316L Stainless Steel in the Concentrated Artifi
Condensate Corrosion Behavior of Type 409 Stainless Steel in Simulated Automotive Muffler Environmen
Intergranular Corrosion of Low Cr Ferritic Stainless Steel 429 Evaluated by the Optimized Double Loo
Effect of post-weld heat treatment on microstructure evolution and pitting corrosion behavior of UNS
Effect of cyclic oxidation on electrochemical corrosion of type 409 stainless steel in the simulated
Effect of temperature, chloride ion and pH on the crevice corrosion behavior of SAF 2205 duplex stai
Influence of Cr-eq/Ni-eq on pitting corrosion resistance and mechanical properties of UNS S32304 dup
Annealing temperature effect on the pitting corrosion resistance of plasma arc welded joints of dupl
Influence of cooling rate on microstructure evolution and pitting corrosion resistance in the simula
Electrochemical impedance spectroscopy investigation on indium tin oxide films under cathodic polari
The mechanism of specific capacitance improvement of supercapacitors based on MnO2 at an elevated op
Effect of Annealing Temperature on the Pitting Corrosion Behavior of UNS S82441 Duplex Stainless Ste
Evaluation of aged duplex stainless steel UNS S32750 susceptibility to intergranular corrosion by op
Influence of the microstructure and alloying element on the polarization behaviour within the crevic
THE INFLUENCE OF SENSITIVE TEMPERATURE ON THE LOCALIZED CORROSION RESISTANCE OF DUPLEX STAINLESS STE
Influence of welding thermal cycles on microstructure and pitting corrosion resistance of 2304 duple
In situ investigation of crevice corrosion on UNS S32101 duplex stainless steel in sodium chloride s
Investigation of selective corrosion resistance of aged lean duplex stainless steel 2101 by non-dest
期刊信息
位置：