中文摘要：

本文通过在新固相源中添加Ni2O3的方法,采用顶部籽晶熔渗生长工艺（TSIG）制备出组分为（1-x）（Gd2O3＋1.2Ba Cu O2）＋x Ni2O3、直径为20 mm的单畴Gd BCO超导块材（其中x=0,0.02,0.06,0.10,0.14,0.18,0.30,0.50 wt%）,并研究了Ni2O3的掺杂量x对样品的表面生长形貌、微观结构、临界温度Tc、磁悬浮力以及俘获磁通密度的影响.研究结果表明,当Ni2O3的掺杂量x在0—0.50 wt%的范围内时,均可制备出单畴性良好的样品,且Ni2O3的掺杂对样品中Gd211粒子的分布和粒径没有明显的影响.在Ni2O3的掺杂量x从0增加到0.50 wt%的过程中,样品的临界温度Tc呈现下降的趋势,从x=0时的92.5 K下降到x=0.50 wt%时的86.5 K,这是由于Ni3＋替代Gd BCO晶体中Cu2＋所致;样品磁悬浮力和俘获磁通密度均呈现先增大后减小的变化规律,x=0.14 wt%时,磁悬浮力达到最大值34.2 N,x=0.10 wt%时,俘获磁通密度达到最大值0.354 T.样品磁悬浮力和俘获磁通密度的变化规律与Ni2O3的掺杂量x有密切关系,只有当掺杂量x合适时,Ni3＋对Cu2＋的替代既不会造成Tc的明显下降,但又能产生适量的Ni3＋/Cu2＋晶格畸变,从而达到提高样品磁通钉扎能力和超导性能的效果.

英文摘要：

Single-domain GdBCO bulk superconductor（20 mm in diameter） has been fabricated by a top-seeding infiltration and growth（TSIG） mathod, it has a new solid phase of [（1- x）（Gd2O3＋1.2BaCuO2） ＋x Ni2O3]（where x = 0, 0.02,0.06, 0.10, 0.14, 0.18, 0.30, 0.50 wt%）. Effect of Ni2O3 additions on the growth morphology, microstructure, critical temperature Tc, magnetic levitation force, and trapped flux of single-domain Gd BCO bulks have been investigated.Results show that the single-domain Gd BCO bulk can be gained when x is in the range of 0–0.50 wt%; and the Gd211 particles are not affected by the Ni2O3 doping in the samples. The Tc of the samples decrease from 92.5 K（x = 0 wt%）to 86.5 K（x = 0.50 wt%） when x increases from 0 to 0.50 wt%, which is caused by the substitution of Ni3＋for Cu2＋.Both of the levitation force and trapped field of the samples increase first and then decrease with the increase of x;the largest levitation force of 34.2 N is obtained for the samples with x = 0.14 wt%, and the largest trapped field of0.354 T is obtained for the samples with x = 0.10 wt%. The change of the levitation force and trapped field of the samples is closely related to the doping content x. As is known, the doping of Ni2O3 can result in substitution of Ni3＋for Cu2＋at its site in Gd BCO crystals, which can reduce the critical temperature Tc of the samples; although Tc and the physical properties of the samples is reduced with the increase in the doping amount of Ni2O3, but at the same time,the substitutions of Ni3＋for Cu2＋in Gd BCO crystals can produce local lattice distortions, which can act as magnetic flux pinning centers to improve the properties of the samples. The highest Tc is obtained in the samples without any Ni2O3additions（x = 0）, but the magnetic flux pinning force of the samples is weak, so both of the levitation force and trapped field of the samples are relatively lower. When the doping content x 0.14 wt%, although the Tc is reduced slightly, it still has a value high