中文摘要：
采用浸渍法制备了三种具有不同载体的锰基NH3低温选择性催化还原（NH3-SCR）催化剂Mn／Ce-ZrO2、Mn／P25和Mn／A12O3。研究了三种催化剂低温SCR脱硝活性及抗H2O、抗SO2性能，并采用XRD、NH3-TPD和H2-TPR手段对催化剂的物理化学性质进行表征。结果表明，在无H2O和SO2存在的情况下，三种催化剂的低温SCR催化活性均比较高。相对来说，Mn／Ce-ZrO2在低温段（100-160℃）活性更高，Mn／P25在高温段（160-220℃）活性更高，这与两种催化剂的氧化还原性质有关。H2-TPR表征表明，Mn／Ce-ZrO2更容易发生氧化还原反应，而Mn／P25还原峰对应的温度较高、面积较大。三种催化剂均有很高的低温抗水性能。另外，Mn／Ce-ZrO2的抗H2O、抗SO2性能最好，而Mn／P25的抗H2O、抗SO2性能最差。Mn／Ce-ZrO2具有较好的抗H2O、抗SO2性能是由于其具有较多的表面酸位点，且表面生成的硫铵盐不稳定。
英文摘要：
Three Mn-based catalysts of Mn/Ce-ZrO2, Mn/P25, and Mrl/A1203 with different supports were prepared by impregnation method and were used in the selective catalytic reduction of NO with NH3（ NH3-SCR） at low temperature. The catalysts were characterized by XRD, NH3-TPD and H2-TPR and their activity at low temperature as well as the resistances towards H2O and SO2 were investigated. The results showed that Mn/Ce- ZrO2 exhibits better activity at low temperature （ 100 - 160 ℃ ） than other two catalysts, while Mn,/P25 performs better at high temperature （160 -220 ℃ ）, which is related with the redox characteristics of the catalysts. Mn/ Ce-ZrO2 is more easily to be reduced at low temperature while Mn/P25 has a larger reduction peak at higher temperature, as revealed by Hz-TPR. All of the three catalysts have a good resistance to H2O; among them Mn/ Ce-ZrO2 exhibits the best resistance to SO2 and H2O, which should be attributed to the abundant acid sites and the instability of ammonia sulfate formed on the surface of Mn/Ce-ZrO2.
同期刊论文项目
同项目期刊论文
A comparative study of Mn/CeO2, Mn/ZrO2 and Mn/Ce-ZrO2 for low temperature selective catalytic reduc
Novel application of biochar from biomass pyrolysis for low temperature selective catalytic reductio
A contrastive study of the introduction of cobalt as a modifier for active components and supports o
Ceria Modified MnOx/TiO2-Pillared Clays Catalysts for Selective Catalytic Reduction of NO with NH3 a
The mechanism of sulfur component in pyrolyzed char from waste tire on the elemental mercury removal
Novel application of cotton stalk as a waste derived catalyst in the low temperature SCR-deNOx proce
Hg2+ Adsorption from a Low-Concentration Aqueous Solution on Chitosan Beads Modified by Combining Po
Alkali metal deactivation of Mn–CeOx/Zr-delaminated-clay for the low-temperature selective catalytic
Mn-0.4/Co0.1Ce0.45Zr0.45Ox, high performance catalyst for selective catalytic reduction of NO by amm
Halloysite-nanotubes supported FeNi alloy nanoparticles for catalytic decomposition of toxic phosphi
Removal of element mercury by medicine residue derived biochars inpresence of various gas compositio
A comparative study of modified cotton biochar and activated carbon based catalysts in low temperatu
期刊信息
位置：