中文摘要：
为了改善La—Mg—Ni系A2B7型电极合金的电化学循环稳定性，用zr部分替代合金中的La,并用熔体快淬工艺制备了La0．75-x Zrx Mg0．25 Ni3．2 Co0．2Al0．1（x=0、0．05、0．1、0．15、0．2）电极合金。用XRD、SEM、TEM分析了铸态及快淬态合金的微观结构，测试了铸态及快淬态合金的电化学循环稳定性，研究了快淬工艺及Zr替代La对合金循环稳定性的影响，探讨了电极合金的失效机理。结果表明，铸态及快淬态合金均具有多相结构，包括两个主相（La，Mg）Ni3及LaNi5和一个残余相LaNi2。快淬处理及Zr替代La可以显著的改善合金的电化学循环稳定性。导致合金失效的主要原因是电极表面被电解液剧烈腐蚀以及合金电极在电化学循环过程中的粉化。
英文摘要：
In order to improve the electrochemical cycle stability of La-Mg-Ni system A2B7-type electrode alloy, La in the alloy was partly substituted by Zr, and the electrode alloys La0.75-x Zrx Mg0.25 Ni3.2 Co0.2Al0.1 （x=0, 0.05, 0.1, 0.15, 0.2） were prepared by melt spinning technology. The structures of the as-cast and spun alloys were analyzed by XRD, SEM and TEM. The electrochemical cycle stability of the alloys was measured. The influences of the melt spinning and substituting La with Zr on the cycle stability of the alloys were investigated in detail. The failure mechanism of the alloy electrodes was investigated. The obtained results indicated that the as-cast and spun alloys have multiphase structure, including two major phases （La, Mg）Ni3 and LaNi5 as well as a residual phase LaNi2. Both the melt spinning and substituting La with Zr significantly improved the electrochemical cycle stability. The fundamental reasons of which cause lose efficacy of the alloy electrodes are that the surface of the alloy electrodes is severely corroded by electrolyte and that the alloy electrodes are pulverized in process of the electrochemical charge-discharge cycle.
同期刊论文项目
同项目期刊论文
Electrochemical hydrogen storage characteristics of nanocrystalline Mg20Ni10-xCux (x=0-4) alloys pre
Microstructure and hydrogen storage characteristics of melt-spun nanocrystalline Mg(20)Ni(10-x)Cu(x)
Hydrogen Storage Behaviours of Nanocrystalline and Amorphous Mg20-xLaxNi10(x=0-6) Hydrogen Storage A
Structures and electrochemical hydrogen storage behaviours of La0.75-xPrxMg0.25Ni3.2Co0.2Al0.1 (x=0-
Improved hydrogen storage behaviours of nanocrystalline and amorphous Mg(2)Ni-type alloy by Mn subst
Enhanced electrochemical characteristics of as-spun nanocrystalline and amorphous Mg(2)Ni-type alloy
Influences of Substitution of Zr for La on Structures and Electrochemical Performances of A(2)B(7)-T
Influence of rapid quenching on hydrogen storage characteristics of nanocrystalline Mg2Ni-type alloy
Investigation on electrochemical performances of melt-spun nanocrystalline and amorphous Mg(2)Ni(1-x
An electrochemical investigation of melt-spun nanocrystalline Mg20Ni10-xCux (x=0-4) electrode alloys
Hydrogenation and dehydrogenation behaviours of nanocrystalline Mg20Ni10-xCux (x=0-4) alloys prepare
Hydrogen storage behaviours of nanocrystalline and amorphous Mg20Ni10-xCox (x=0-4) alloys prepared b
Electrochemical hydrogen storage characteristics of nanocrystalline and amorphous Mg20Ni10-xCox (x=0
Hydriding and dehydriding characteristics of nanocrystalline and amorphous Mg20-xLaxNi10(x=0-6) allo
An electrochemical investigation of melt-spun nanocrystalline and amorphous Mg2Ni-type electrode all
Hydriding and dehydriding characteristics of nanocrystalline and amorphous Mg20Ni10-xCox (x=0-4) all
Investigation on the structures and electrochemical performances of La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1
An investigation on the hydrogen storage characteristics of the melt-spun nanocrystalline and amorph
Structures and electrochemical cycle stability of La0.75-xPrx Mg0.25Ni3.2Co0.2Al0.1 (x=0-0.4) alloys
Effects of rapid quenching on the structures and electrochemical characteristics of the La0.5Ce0.2Mg
Structures and electrochemical hydrogen storage behaviours of La0.75-xPrxMg0.25Ni3.2Co 0.2A 0.1 (x =
Structures and electrochemical cycle stability of La0.75?xPrxMg0.25Ni3.2Co0.2Al0.1 (x = 0–0.4) alloy
Investigation on the structures and electrochemical performances of La0.75?xZrxMg0.25Ni3.2Co0.2Al0.1
Influence of the substituting Ni with Fe on the cycle stabilities of as-cast and as-quenched La0.7Mg
Influence of spark plasma sintering temperature on electrochemical performance of La0.80Mg0.20Ni3.75
Effect of cobalt content on electrochemical performance of La-Mg-Ni system (Ce2Ni7-type) electrode a
期刊信息
位置：