中文摘要：
用快淬工艺制备了纳米晶和非晶Mg2Ni型Mg2Ni1-xMnx（x=0、0.1、0.2、0.3、0.4）合金,获得长度连续,厚度约为30μm,宽度约为25mm的薄带。用XRD、HRTEM分析了快淬合金薄带的微观结构,测试了合金薄带的电化学性能及电化学交流阻抗谱（EIS）,测试了电位阶跃后的阳极电流-时间相应曲线,并计算了氢在合金中的扩散系数（D）。结果表明,快淬无Mn合金均具有典型的纳米晶结构,而快淬含Mn（x=0.4）合金显示了纳米晶和非晶结构,这证实Mn替代Ni有利于Mg2Ni型合金形成非晶相。Mn替代Ni及快淬处理显著地改善了合金的电化学贮氢性能,包括放电容量和电化学循环稳定性。合金的高倍率放电能力（HRD）随淬速的增加而单调上升,但随Mn替代量的变化HRD具有极大值。
英文摘要：
The Mg2Ni-type Mg2Ni1-xMnx（x=0,0.1,0.2,0.3,0.4） alloys with a nanocrystalline and amorphous structure are synthesized by melt-spinning technique.The as-spun alloy ribbons with a continuous length,a thickness of about 30μm and a width of about 25mm are obtained.The structures of the as-spun alloy ribbons were characterized by XRD and HRTEM.The electrochemical characteristics as well as the electrochemical impedance spectrums（EIS） of the as-spun alloy ribbons are measured.The semilogarithmic curves of anodic current versus time responses of the alloy were plotted by an electrochemical workstation,and the hydrogen diffusion coefficients（D） in the alloys were obtained by virtue of potential-step method.The results show that all the as-spun alloys（x=0） hold typical nanocrystalline structure,whereas the as-spun alloy（x=0.4） displays a nanocrystalline and amorphous structure,confirming that the substitution of Mn for Ni facilitates the glass formation in the Mg2Ni-type alloy.The substitution of Mn for Ni significantly improves the electrochemical performances of the alloys,involving the discharge capacity and the electrochemical cycle stability.The high rate dischargeability（HRD） of the alloy monotonously grows with increasing the spinning rate,but it obtains a maximum value with the variation in the percent of Mn substitution.
同期刊论文项目
同项目期刊论文
Electrochemical hydrogen storage characteristics of nanocrystalline Mg20Ni10-xCux (x=0-4) alloys pre
Microstructure and hydrogen storage characteristics of melt-spun nanocrystalline Mg(20)Ni(10-x)Cu(x)
Hydrogen Storage Behaviours of Nanocrystalline and Amorphous Mg20-xLaxNi10(x=0-6) Hydrogen Storage A
Structures and electrochemical hydrogen storage behaviours of La0.75-xPrxMg0.25Ni3.2Co0.2Al0.1 (x=0-
Improved hydrogen storage behaviours of nanocrystalline and amorphous Mg(2)Ni-type alloy by Mn subst
Enhanced electrochemical characteristics of as-spun nanocrystalline and amorphous Mg(2)Ni-type alloy
Influences of Substitution of Zr for La on Structures and Electrochemical Performances of A(2)B(7)-T
Influence of rapid quenching on hydrogen storage characteristics of nanocrystalline Mg2Ni-type alloy
Investigation on electrochemical performances of melt-spun nanocrystalline and amorphous Mg(2)Ni(1-x
An electrochemical investigation of melt-spun nanocrystalline Mg20Ni10-xCux (x=0-4) electrode alloys
Hydrogenation and dehydrogenation behaviours of nanocrystalline Mg20Ni10-xCux (x=0-4) alloys prepare
Hydrogen storage behaviours of nanocrystalline and amorphous Mg20Ni10-xCox (x=0-4) alloys prepared b
Electrochemical hydrogen storage characteristics of nanocrystalline and amorphous Mg20Ni10-xCox (x=0
Hydriding and dehydriding characteristics of nanocrystalline and amorphous Mg20-xLaxNi10(x=0-6) allo
An electrochemical investigation of melt-spun nanocrystalline and amorphous Mg2Ni-type electrode all
Hydriding and dehydriding characteristics of nanocrystalline and amorphous Mg20Ni10-xCox (x=0-4) all
Investigation on the structures and electrochemical performances of La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1
An investigation on the hydrogen storage characteristics of the melt-spun nanocrystalline and amorph
Structures and electrochemical cycle stability of La0.75-xPrx Mg0.25Ni3.2Co0.2Al0.1 (x=0-0.4) alloys
Effects of rapid quenching on the structures and electrochemical characteristics of the La0.5Ce0.2Mg
Structures and electrochemical hydrogen storage behaviours of La0.75-xPrxMg0.25Ni3.2Co 0.2A 0.1 (x =
Structures and electrochemical cycle stability of La0.75?xPrxMg0.25Ni3.2Co0.2Al0.1 (x = 0–0.4) alloy
Investigation on the structures and electrochemical performances of La0.75?xZrxMg0.25Ni3.2Co0.2Al0.1
Influence of the substituting Ni with Fe on the cycle stabilities of as-cast and as-quenched La0.7Mg
Influence of spark plasma sintering temperature on electrochemical performance of La0.80Mg0.20Ni3.75
Effect of cobalt content on electrochemical performance of La-Mg-Ni system (Ce2Ni7-type) electrode a
期刊信息
位置：