采用超声速等离子喷涂技术在45钢基体上制备NiCrBSi合金涂层,涂层整体结构致密,含有少量微缺陷。使用球盘式接触疲劳试验机在接触应力为1.86 GPa,转速为1 500 r/min的条件下对涂层试样进行接触疲劳试验,得到涂层的接触疲劳寿命为9.0×105周次;同时建立Weibull失效概率图,通过该图可以直观地得到在同一工作条件下,涂层任意循环次数的失效概率。测量涂层不同疲劳阶段的残余应力,结果表明：一旦进行接触疲劳试验,其残余应力形式由拉应力迅速转化为压应力,在整个疲劳过程的前半段,应力增强较为缓慢,在疲劳过程的后半段,应力值迅速增大,疲劳过程的中期成为了应力变化的转折点。根据这一规律,可以有效地判定涂层处于疲劳过程的哪个阶段,从而为预防涂层的突然失效提供了一种新的手段。
英文摘要：
The NiCrBSi alloy coating is deposited on steel（AISI 1045） substrates using supersonic plasma spraying technique.The overall structure of the coating is densification and contained a small amount of micro-defects.Rolling contact fatigue（RCF） life of the coating is investigated using a ball-on-disc tester under 1.86 GPa contact stress,and 1 500 r/min rotation velocity.Obtained that the contact fatigue lifetime of coating is 9.0×105 cycle,map of Weibull distribution failure probability is plotted as well.And the failure probability of random cycle is achieved by this Weibull plot under identical work condition.Coating＇s residual stress at stage of fatigue life is measured by the X-ray equipment.The results show that the residual stress changed by tensile stress into compressive stress when contact fatigue tests start,and the stress rises slowly in the first half of fatigue process while increases sharply in the following procedure,which makes the mid-stage became the critical point of fatigue failure process.Following this law,fatigue stage of coating can be determined,and the catastrophic failure of coating can be prevented effectively.
同期刊论文项目
同项目期刊论文
Health condition monitoring with multiple physical signals including micro resistance, infrared ther
Microstructure and nanoindentation measurement of residual stress in Fe-based coating by laser cladd
Investigation of a novel rolling contact fatigue/wear competitive life test machine faced to surface
Research on the microstructure and space tribology properties of electric-brush plated Ni/MoS2-C com
Influence of surface nitriding treatment on rolling contact behavior of Fe-based plasma sprayed coat
On the evaluation of residual stress and mechanical properties of FeCrBSi coatings by nanoindentatio
Influence of loading levels on RCF life and failure mode of Ni-based alloy and WC-Ni ceramic composi
Investigation of novel rolling contact fatigue/wear competitive life test machine faced to surface c
Excellent vacuum tribological properties of Pb/PbS film deposited by Rf magnetron sputtering and ion
Bimodal distribution characteristic of microstructure and mechanicalproperties of nanostructured com
Measurement for mechanical behavior and fatigue property of Cu films by nanoscale dynamic load metho
An experimental analysis of fatigue behavior of a welded impeller made byFV520B stainless steel in a
Investigation on influence of WC–Ni addition on rolling contact fatigue behavior of plasma sprayed N
Structural integrity and ferroelectric-piezoelectric properties of PbTiO3 coating prepared via super
The dependency of microstructure and mechanical properties of nanostructured alumina-titania coating
Reseach on the microstructure and space tribology properties of electric-brush plated Ni/MoS2-C comp
Structure and wear behavior of NiCr-Cr3C2 coatings sprayed by supersonic plasma spraying and high ve
Microstructure and nanoindentation measurement of residual stress in Fe-base coating by laser claddi
Effects of argon gas flow rate on the microstructure and micromechanical properties of supersonic pl
Competing failure mechanism and life prediction of plasma sprayed composite ceramic coating in rolli
Failure process analysis of plasma sprayed coatings under tip load based on acoustic emission signal
The tribological behavior of glass fiber-reinforced polyetheretherketone composite under dry sliding
Effects of service condition on rolling contact fatigue failure mechanism and lifetime of thermal sp
Health condition monitoring with multiple physical signals in the fatigue test for double-material f
Characterization of microstructure and rolling contact fatigue performance of NiCrBSi/WC-Ni composit
Investigation of fatigue failure prediction of Fe-Cr alloy coatings under rolling contact based on a
Effects of surface nanocrystallization pretreatment on low-temperature ion sulfurization behavior of
Indentation Size Effect on the Mechanical Properties of Supersonic Plasma Sprayed NiCr-Cr3C2 Coating
Accelerated fatigue life testing of NiCr-Cr3C2 coating at different loads under rolling contact cond
期刊信息
位置：