采用蒸发—冷凝法在真空条件下制备了片状Cu粉,并用激光粒度分析仪（SL）、扫描电镜（SEM）、辉光放电质谱仪（GDMS）和X射线衍射仪（XRD）对片状Cu粉进行表征。结果表明,制备的Cu粉为面心立方结构,表面平整,分散性好,粒径为10~30μm,厚1~2μm。试验考察了蒸发温度、真空度、保温时间和冷凝高度4个因素对片状Cu粉粒径和形貌的影响,发现蒸发温度和真空度对蒸发速率有较大影响;探讨了Cu粉颗粒的形成机制。
英文摘要：
The flake copper powder was prepared by the evaporation and condensation in vacuum,and characterized by laser particle size analyzer（SL）,scanning electron microscopy（SEM）,glow discharge mass spectrometry（GDMS） and X-ray diffraction（XRD）.The results reveal that the copper powders are of face-center-cubic structure,with even surface and uniform shape,and dispersed well.The average particle size is 10～30μm,the thickness of the flake copper powder is about 1～2μm.The influence of evaporating temperature,vacuum degree,holding time and condensation distance on particle size and morphology was investigated.Results show that evaporating rate is effected by evaporating temperature and vacuum degree.The formation mechanism of Cu particles was discussed.
同期刊论文项目
同项目期刊论文
Thermodynamic calculation and experimental investigation on the products of carbothermal reduction o
Preparation of titanium carbon powders by carbothermal reduction of titanium/charcole at vacuum cond
期刊信息
位置：