中文摘要：

以漆酚为基体，石墨为导电填料，利用紫外光固化法制备漆酚／石墨复合导电涂料，讨论了涂膜中石墨的含量以及固化方式等对漆膜导电性能的影响，并测试了漆膜的常规物理机械性能。结果表明，在紫外光辐照下，漆酚／石墨混舍物涂膜可快速固化。当石墨含量达到25％（wt％）时，漆膜的表面电阻率为442Ω．cm，硬度为6H，附着力2级，冲击强度为45kg．cm。

英文摘要：

Polyumshiol/graphite composite conductive coating was prepared by UV irradiation, the effect of coneentration of graphite and curing method on electrical resistvity of composite film were studied. Physico - mechanical properties of polyurushiol/graphite composite film was also discussed. The results show that urushiol/graphite com- posite film was cured by UV irradiation. And the surface resistivity dropped shaply as the loading of graphite is 25%. The surface resistivity value is 442Ω. cm with 6H hardness of, 2 adhesion of and 45kg. em impact strength of.