中文摘要：
采用水热反应釜法制备碳量子点以及氯化亚砜功能化碳量子点,然后分别与用乙二醇还原的银纳米粒子进行混合,制成复合催化剂。利用FTIR、TEM对样品进行表征,利用荧光分光光度计测试荧光谱,紫外-可见分光光度计测试吸收谱和甲基橙浓度。结果表明：碳量子点的平均粒径约3.5 nm,类球形银纳米粒子的平均粒径约18 nm。银纳米粒子和碳量子点复合催化剂能够使荧光猝灭,使可见光区的吸收增强。复合催化剂比单独的银纳米粒子和碳量子点的催化能力更好。银纳米粒子和碳量子点以体积比为1：2的比例复合时催化效率最高。氯化亚砜功能化的碳量子点与银纳米粒子复合能提高降解甲基橙的浓度和降解速率,降解完50 mg/L,50 mL的甲基橙仅需12 min。
英文摘要：
Orignal CQDs and functionalized CQDs with SOCl_2（Cl-CQDs） were prepared in an autoclave, and silver nanoparticles were synthesized using ethylene glycol as a reducing agent. Ag/CQDs and Ag/Cl-CQDs were synthesized by simple mixing. The samples were detected by TEM and FTIR. Fluorescence and absorption spectra were recorded on a fluorescence spectrophotometer and UV-Vis spectrometer, respectively. The results show that the average diameter of CQDs is about 3.5 nm, and the mean diameter of roundish silver nanoparticles is about 18 nm. Fluorescence quenching happens after incorporating Ag into CQDs, and absorption capacity is strengthened in the visible light wavelength range. The photocatalytic property of the composite catalysts is stronger than that of single Ag and CQD.The composite catalyst with a volume ratio of Ag/CQDs of 1/2 has the highest catalytic efficiency. Ag/Cl-CQDs can promote the degradation of methyl orange, and 50 m L, 50 mg/L methyl orange is degraded in 12 min.
同期刊论文项目
同项目期刊论文
Ba0.6Sr0.4TiO3-MgO ceramics from ceramic powders prepared by improved aqueous gelcasting-assisted so
Effects of Sn substitution on structural and electrical properties of BaSn0.75M0.25O3-δ (M = Sc, In,
Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as p
Effects of foam composition on the microstructure and piezoelectric properties of macroporous PZT ce
Properties of Alumina Coagulated Bodies Prepared by Direct Coagulation Casting via High Valence Coun
Carbon-Dot-Loaded Alginate Gels as Recoverable Probes: Fabrication and Mechanism of Fluorescent Dete
Direct coagulation casting of alumina using magnesium citrate as coagulating agent with glycerol dia
Direct Coagulation Casting of Positively Charged Alumina Suspension by Controlled Release of High Va
Microstructure characteristics of blue-and-white porcelain from the folk kiln of Ming and Qing Dynas
Preparation of Al2O3 poly-hollow microsphere (PHM) ceramics using Al2O3 PHMs coated with sintering a
Enhanced piezoelectric properties of PZT ceramics prepared by direct coagulation casting via high va
Preparation of porous Si3N4 ceramics via tailoring solid loading of Si3N4 slurry and Si3N4 poly-holl
Synthesis, microstructure and electrical properties of BaZr0.9Y0.1O3-delta: BaCe0.86Y0.1Zn0.04O3-del
Direct coagulation casting of yttria-stabilized zirconia using magnesium citrate and glycerol diacet
Direct Coagulation Casting of Alumina Suspension by High Valence Counter Ions Using Ca(IO3)2 as Coag
Pore morphology designs of porous Si3N4-based ceramics using Si3N4 and Al2O3 poly-hollow microsphere
Chlorine-functionalized carbon dots for highly efficient photodegradation of pollutants under visibl
Self-assembly of fluorescent carbon dots in a N,N-dimethylmethanamide solution via Schiff base react
Effect of calcining temperature of Si3N4 poly-hollow microspheres on the properties of the porous Si
Enhanced performance of Fe3+ detection via fluorescence resonance energy transfer between carbon qua
Effect of sintering temperature on properties of porous Si3N4 ceramics with Si3N4 poly-hollow micros
期刊信息
位置：