中文摘要：
腐蚀电位监测、线性极化和交流阻抗测试等方法研究混凝土中添加萘系减水剂对钢筋腐蚀行为的影响．发现添加萘系减水剂的混凝土，其电阻和极化电阻大幅增加，其中以添加0．2％萘系减水剂的增幅最明显．适量的萘系减水剂有利于改善混凝土的孔隙结构，增强混凝土的密实性和抗渗透性能，从而减缓混凝土的钢筋腐蚀．
英文摘要：
The influence of naphthalene water reducer on corrosion behavior of reinforcing steel in concrete was studied by the methods of corrosion potential measurement, linear polarization and EIS test. The values of concrete resistance （ Rc ） and polarization resistance （ Rp ） of the samples with naphthalene water reducer were higher than those without naphthalene water reducer, especially in the concrete with 0.2 percent naphthalene water reducer. A suitable amount of water reducer can improve the pore structures of concrete, increase the concrete compactness and impermeability, and decrease corrosion rate of rebars in concrete.
同期刊论文项目
同项目期刊论文
The influence of Ce(NO3)3.6H2O on the of inhibitive Effect of Ca(NO2)2 IN Simulated Concrete Pore So
Corrosion behavior of steel in simulated concrete pore solutions treated with calcium silicate hydra
Study on interaction between macrocell and microcell in the early corrosion process of reinforcing s
A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using sc
Study on the corrosion behavior of reinforcing steel in simulated concrete pore solutions using in s
The Electrochemical Characteristics of Pitting for Two Steels in Phosphate Buffer Solution with Chlo
Corrosion behavior of reinforcing steel in simulated concrete pore solutions: A scanning micro-refer
Corrosion initiation of stainless steel in HCl solution studied using electrochemical noise and in-s
A Phtoelectrochemical Study of Highly Ordered TiO2 Nanotube Arrays as the Photoanodes for Cathodic P
The degradation of passive film on carbon steel in concrete pore solution under compressive and tens
Effective monitoring of corrosion in reinforcing steel in concrete constructions by a multifunctiona
位置：