中文摘要：
通过研究化学钢化前、钢化后钠钙玻璃的压痕形貌、几何尺寸和表面力学性能，分析和探讨了表面残余应力对玻璃压痕参数以及表面力学性能变化的影响机理。结果表明，普通玻璃的压痕与钢化玻璃的压痕有明显的差别，钢化玻璃的压痕周围呈圆形放射状光斑，压痕裂纹很小，其硬度值比相同载荷下钢化前玻璃硬度值增加了约15．8％，压痕断裂韧性有明显的提高，是钢化前玻璃断裂韧性的2．75倍，显示了钢化后表面残余压应力对玻璃的压痕参数和力学性能的影响。
英文摘要：
Vickers indentations on soda-lime glasses before and after chemically strengthening were investigated for understanding the influence of the residual stresses on the mechanical properties. It was found that a circle bright zone was generated slowly around the indent in the strengthened glass. Under the same loading, the measured hardness of the strengthened glass increases approximately 15.8% than that of common soda-lime glass, and the fracture toughness is almost 2.75 times of the common glass. The mechanism of residual stress on the indentation and the mechanical properties has been analyzed and discussed.
同期刊论文项目
同项目期刊论文
A Simple Methods for Measuring Tensile and Shear Band Strength and for Determining Elastic Modulus a
Simple Methods for Measuring Band Strength and for Determining Elastic Modulus and Strength of Coati
Effects of strain hardening and residual stress in impression on the instrumented indentation techni
Influence of stress parallel to crack plan on subcritical crack propagation in glass under biaxial s
Assessing the elastic parameters and energy-dissipation capacity of solid materials: A residual inde
Anisotropic deformation and damage behavior of brittle-ductile laminated composites in bending at hi
Investigation in biaxial-stress effect on mode I fracture resistance of brittle materials by FEM sim
Investigation of the relationship between elastic modulus and hardness based on depth-sensing indent
Mechanism for the enhanced oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid soluti
期刊信息
位置：