中文摘要：

在钢铁工业的节能减排形势下,首钢开展了高炉高风温试验研究。2009年高风温试验情况表明,迁钢2号高炉连续4个月月均风温突破1 270℃,实现年均风温1 258.7℃,达到了高炉生产降低焦比和提高煤比等目标。采用对比分析法总结分析了高风温试验前、2008年和2009年迁钢2号高炉的试验数据,2009年实现1 280℃高风温下的热风炉、高炉等操作技术,研究了助燃空气温度、煤气预热温度、煤气热值、煤气流量和燃烧送风时间等参数对高风温的影响,提出了高风温随其影响参数的变化规律。

英文摘要：

With the situation of energy-saving and emission reduction in steel industry,commerical test of high blast temperature in Shougang was carried out in 2009.The results show that,monthly average blast temperature on Qiangang′s No.2 blast furnace breaks through 1 270 ℃ for four months continuously,yearly average blast temperature about 1 258.7 ℃ is realized,the aim to lower coke ratio and high coal ratio of blast furnace production is obtained.Operative technique of hot blast stove and blast furnace in high blast temperature to reach 1 280 ℃ on Qiangang′s No.2 BF in 2009 was summarized and analyzed with contrast analysis method,effect of parameters such as combustion-supporting air temperature,preheated gas temperature,gas heat value,gas flux,combustion and blast time on high blast temperature,and the change laws of high blast temperature with its impact factor were put forward.