利用透射电子显微镜对质子辐照前后空间太阳望远镜Mo/Si多层膜的微观结构进行了表征,并对其辐照前后反射率的变化进行了测量.研究表明,Mo/Si多层膜经质子辐照后形成了一些缺陷结构,局部区域Mo/Si的周期性遭到破坏,Mo层与si层的宽度发生了变化,多层膜层与层之间的界面也比辐照前更为粗糙,部分层状结构由于质子辐照发生了明显的扭曲和折断等现象;此外,质子辐照导致了Mo/Si多层膜反射率的下降,这些微观缺陷的形成是光学性能降低的直接诱因.
英文摘要：
In this paper we characterize the microstructures of Mo/si multilager in space solar telescope induced by proton irradiation by transmission electron microscope（TEM）.The optical performances of the Mo/Si multilayer mirror before and after proton irradiation are also determined.The experimental results show that some defect structures are introduced after proton irradiation.The Mo/Si periodic structure is destructed in some irradiation regions.The widths of Mo layer and Si layer significantly change and the Mo/Si interface is much rougher than before irradiation.Moreover,the obvious distortions of the Mo/Si interface and the formation of the small islands in Mo layer are also found.Furthermore,proton irradiation reduces the reflectivity of Mo/Si multilayer mirror.The dominante mechanism of optical degeneration of the Mo/Si multilayer induced by proton irradiation should be attributed to the formation of the defect structures.
同期刊论文项目
同项目期刊论文
Theoretical Analysis and Experimental Measurement for Secondary Electron Yield of Microchannel Plate
Defects and Microstructures in the Surface Layer of Single-crystal Silicon Induced by High-current P
Calculation of quantum efficiency of alkali halide photocathode materials in the extreme ultraviolet
Fabrication of Micropore on AISI 304L Austenitic Stainless Steel Surface by High-current Pulsed Elec
Effect of vacancy defect clusters on the optical property of the aluminium filter used for the space
The vacancy defect clusters in polycrystalline pure aluminum induced by high-current pulsed electron
Mechanism of surface nanocrystallization in pure nickel induced by high-current pulsed electron beam
Physical model of stress and deformation microstructures in AISI 304L austenitic stainless steel ind