中文摘要：
研究了标准养护7 d碱含量不同的水泥砂浆在相对湿度为33%、55%和79%三种不同湿度环境下的水分扩散和干燥收缩规律。结果表明,随着相对湿度的降低,水泥基材料的干燥失水和收缩值均增大;KOH掺量在0.5%~1.5%（占水泥质量百分比）范围内时,加快水泥基材料的水分损失,但促进作用有限;在相对湿度分别为33%与55%且KOH含量小于1.5%和相对湿度为79%且KOH含量小于1.0%时,碱也能够促进水泥基材料的干燥收缩。
英文摘要：
The law of moisture diffusion and drying shrinkage of cement mortar with different alkali content and which had been cured in the humid room for 7 days were studied in different relative humidity of 33%、55% and 79%.The results show that with the decreased relative humidity,the water loss and shrinkage increased.It also shows that the development speed of water loss of cement-based materials could be promoted when the content of KOH is 0.5%～1.5%（accounting for percentage of cement mass）,but with limited promotion function.The drying shrinkage can also be promoted by alkali in two cases,one is that the respective relative humidity is 33% and 55% respectively and the content of KOH is below 1.5%,and the other is that the relative humidity is 79% and the content of KOH is below 1.0%.
同期刊论文项目
同项目期刊论文
Service Life Prediction of Lining Concrete of Subsea Tunnel under Combined Compressive Load and Carb
Visualization and quantification of water movement in porous cement-based materials by real time the
Observation and quantification of water penetration into strain hardening cement-based composites (S
Observation and quantification of water penetration into frost damaged concrete by neutron radiograp
Penetration of water into uncracked and cracked steel reinforced concrete elements, visualization by
Observation of Water Penetration into Water Repellent and Cracked Cement-based Materials by Means of
Neutron radiography, a powerful method to determine time-dependent moisture distributions in concret
位置：