中文摘要：
以Ni为催化剂、乙烯作碳源，制备了纳米碳纤维／蜂窝状堇青石催化剂载体，并考察了制备工艺对所制纳米碳纤维（CNFs）产率及形貌的影响。结果表明：当生长温度从450℃升至650℃时，CNFs的产率先增加后降低；当生长时间由5rain延长至30min时，CNFs的产率从4．9％提高到12．5％，随着生长时间的进一步延长，增长趋于平缓；较高的C2H4／H2流量比有利于提高CNFs的产率；在500℃、30min、VC2H4：VH2=160：40的最佳工艺条件下，CNFs的产率及所制载体的压缩强度分别达12．5％和34．46MPa。
英文摘要：
As catalyst carriers, carbon nanofibers （CNFs） were grown on A120：~-coated cordierite monolith by using Ni as catalyst and ethylene as carbon source. The effect of growth conditions on the yield and morphology of CNFs was investigated. Results show that at the temperature range of 450 -650 ℃, the yield of synthesized CNFs increases with increasing growth temperature from 450 ℃ to 550 ℃ but decreases with further increasing growth temperature to 650 ℃. With increasing growth time from 5 min to 30 min, the CNFs yield increases from 4.9% to 12.5%, while the growth of CNFs is leveled out after 30 min. The yield of CNFs is improved by increasing volume ratio of C2 H4 to H2 in the feed gas. Under the optimal growth conditions with VC2H4 - VH2 =160 ： 40 at 500 ℃ for 30 min, the yield of synthesized CNFs reaches 12.5 %, and the CNFs/cordierite monolith obtained exhibits a compressive strength of 34.46 MPa.
同期刊论文项目
同项目期刊论文
The superior electrochemical performance of oxygen-rich activated carbons prepared from bituminous c
Molecular design of polymer precursors for controlling microstructure of organic and carbon aerogels
Effect of template and precursor chemistry on pore architectures of triblock copolymer-templated mes
Influence of nitrogen hetero-substitution on the electrochemical performance of coal-based activated
Fabrication of hierarchical porous carbide-derived carbons by chlorination of mesoporous titanium ca
Hollow carbon spheres with encapsulation of Co3O4 nanoparticles as anode material for lithium ion ba
LiFePO4/C nanocomposites synthesized from Fe2O3 by a hydrothermal reaction-calcination process and t
Structure control of V2O5/CNFs/cordierite monolith catalyst and its catalytic performance on NO remo
MnOx-CeO2/activated carbon honeycomb catalyst for selective catalytic reduction of NO with NH3 at lo
A high strength carbon nanofiber/honeycomb cordierite composite produced by chemical vapor depositio
Modification of polystyrene-based activated carbon spheres to improve adsorption of dibenzothiophene
Low-Temperature Selective Catalytic Reduction of NO with Urea Supported on Pitch-Based Spherical Act
期刊信息
位置：