中文摘要：

为了有效去除富氢重整气体中少量的CO,将4Ni-2Ru／ZrO2双金属催化剂均匀涂布到微通道反应器中，运用CO选择性甲烷化方法来净化CO．考察了焙烧温度、催化剂的涂布方法、CTAB／Zr摩尔比和空速对催化剂性能的影响．实验结果表明：CTAB／Zr的摩尔比为0．35、空速为14286h～、每次涂布催化剂浆液后350℃下焙烧时，所制备的催化剂表现出良好的低温活性，反应温度为260℃时可将CO的出口含量降低到0．0013％（体积分数）；CTAB／Zr摩尔比为0．35、每次涂布浆液后350℃下焙烧的催化剂，适宜的空速范围为13000～20000h^-1。

英文摘要：

In order to effectively remove the small-quantity CO in hydrogen-rich reformed gas, 4Ni-2Ru/ZrO2 bimetallic catalyst was homogeneously coated on a microchannel reactor, and the method of selective methanation was used to purify CO. Then, the effects of calcination temperature, coating method, CTAB/Zr molar ratio and space velocity on the catalyst performance were investigated. Experimental results show that （1） when the calcination is performed at 350℃ after each slurry loading with a CTAB/Zr molar ratio of 0.35 and with a space velocity of 14286 h- 1, 4Ni-2Ru/ZrO2 catalyst is of excellent performance in low temperature, and the volume fraction of CO at the outlet reduces to 0. 0013 % at 260 ℃; and （2） a space velocity of 13000 -20000 h- 1 is suitable for the catalyst calcined at 350 ℃ after each slurry loading with a CTAB/Zr molar ratio of 0.35