中文摘要：
以2，2-双[4～（4-氨基苯氧基苯基）]六氟丙烷（BDAF）为二胺单体，均苯四酸二酐（PMDA）为二酐单体，采用两步法制备了BDAF—PMDA型聚酰亚胺，进一步高温热解制备炭膜．采用红外、热重、X射线衍射分析其结构变化，并测试炭膜对纯组分及混合气体的渗透性能和分离选择性．结果表明，BDAF-PMDA型炭膜具有较高的气体渗透性，在CO2／H2体系中可优先渗透CO2．提高炭化温度，炭膜孔径减小，气体的渗透性能降低，选择性提高，并使得BDAF-PMDA型炭膜的分离机理由表面扩散为主逐渐变为表面扩散和分子筛分共同控制．
英文摘要：
The BDAF-PMDA polyimide which synthesized with the monomer of pyromellitic acid dianhydride and 2,2-Bis [4-（4-aminophenoxy）phenyl]-hexafluoropropanane by two step method was used to prepare the carbon membrane by the pyrolysis at the high temperature. The changes of chemical structure of BDAF-PMDA polyimide during the pyrolysis and gas separation properties of derived carbon membranes were characterized by FTIR, TG, XRD, and gas permeation tests of pure and mixed gas. Results indicate that the carbon membrane prepared from the BDAF-PMDA polyimide precursor exhibits the higher gas permeability for small gas molecules, especially for CO2 which can be permeated faster than Hz in the mixture of CO2/H2. With the increase of carbonization temperature, the pore size of carbon membrane decreases. As a result, the gas permeability of the derived carbon membrane is reduced and the gas selectivity is enhanced. And the separation mechanism of BDAF-PMDA carbon membrane is changed from the surface diffusion mechanism into the coexistence of surface diffusion and molecular sieving mechanism.
同期刊论文项目
同项目期刊论文
Comparison study of the effect of PVP and PANI nanofibers additives on membrane formation mechanism,
Visualization of the Formation of Interfacially Polymerized Film by an Optical Contact Angle Measuri
Novel tertiary amino containing thin film composite membranes prepared by interfacial polymerization
Performance Improvement of Polysulfone Ultrafiltration Membrane Using Well-Dispersed Polyaniline-Pol
An Effective Method to Improve the Performance of Fixed Carrier Membrane via Incorporation of CO2-se
Gas separation performance of C/CMS membranes derived from poly(furfuryl alcohol) (PFA) with differe
Preparation of dual-layer cellulose/polysulfone hollow fiber membrane and its performance for isopro
An antioxidative composite membrane with the carboxylate group as a fixed carrier for CO2 separation
High performance antioxidative and acid resistant membrane prepared by interfacial polymerization fo
Improvement of CO2/N-2 separation characteristics of polyvinylamine by modifying with ethylenediamin
Performance improvement of polysulfone ultrafiltration membrane using PANiEB as both pore forming ag
High-performance membranes comprising polyaniline nanoparticles incorporated into polyvinylamine mat
Formation-structure-performance correlation of thin film composite membranes prepared by interfacial
Effects of Curing Method on the Gas Separation Performance of Phenolic Resin/Poly(vinyl Alcohol)-Bas
Gas separation performance of C/CMS membranes derived from poly (furfuryl alcohol) (PFA) with differ
Effects of precursor preoxidization on the structure and gas separation properties of polyetherimide
Preparation of C/CMS composite membranes derived from Poly(furfuryl alcohol) polymerized by iodine c
Controlled synthesis of high performance carbon/zeolite T composite membrane materials for gas separ
期刊信息
位置：