中文摘要：
采用铸锭冶金法制备了含稀土La的Al-Mg-Zr合金,通过金相显微镜、扫描电镜、能谱和X射线衍射及力学性能测试,观察分析了0.2%的La微合金化对Al-5Mg-0.2Zr合金微观组织和力学性能的影响。结果表明,在Al-5Mg-0.2Zr合金中添加0.2%的La能显著细化合金晶粒,合金的平均晶粒尺寸下降到68μm,同时有效地避免了Al3Zr析出相的粗化和偏聚,使合金抗拉强度、屈服强度及伸长率分别增加到了165.5MPa、112.5MPa和7.5%。
英文摘要：
Al-Mg-Zr alloys containing La elements were prepared by cast metallurgy. Effects of 0.2 % La additions on mierostructure and mechanical properties of Al-5Mg-0.2Zr alloy were investigated by tensile testing, optical microscopy （OM）, scanning electron microscopy （SEM）, energy spectrum （EDS） and X-ray diffraction （XRD）. The results show that the addition of 0.2% La can positively refine the grain size of Al-5Mg-0.2Zr alloy and effectively avoid the coarsening and segregation of AI3Zr in the matrix, and the average grain size of the alloy is decreased to only 68μm. Meanwhile, the tensile strength, yield strength and elongation are increased to 165.5 MPa,112.5 MPa and 7.5%, respectively.
同期刊论文项目
同项目期刊论文
Effect of Inoculants Ti and Zr on Microstructure and Mechanical Properties of 2519 Al-Cu Alloy Welds
Effect on LY12 aluminum alloy welding joint microstructure and properties with Electron Beam Welding
Effect of compound inoculants Ti and Zr on as cast microstructure and mechanical properties of Al-Cu
Study on the microstructure and properties of resistance spot welding joint for ultra fine-grained s
Effect of rotary direction and speed on mechanical properties in friction stir spot welding of A6061
Microstructure and mechanical property of multi-walled carbon nanotubes reinforced aluminum matrix c
Effect of plunge speeds on hook geometries and mechanical properties in friction stir spot welding o
Microstructure and Mechanical Properties of Aer Met 100 Ultra-high Strength Steel Joints by Laser We
期刊信息
位置：