中文摘要：
以B2O3为原料，Al粉为还原剂，用KCl03做助燃剂，通过自蔓延铝热还原制备硼粉，研究KCl03添加量（质量分数）及反应物料B2O3与Al粉的配比对产物纯度的影响，利用X射线衍射（XRD）、扫描电镜（SEM）和能谱仪（EDS）对产物进行物相、形貌和元素分析。结果表明：还原产物主要由α-B及少量A1、B203和α-Al2O3组成；随着助燃剂KClO3添加量增加，产物中B含量w（B）逐渐增多，Al含量w（Al）逐渐减少。当KCl03添加量（质量分数）为25％时，w（B）最高为94．38％，w（Al）为5．62％；随着反应体系中A1含量减少，产物纯度呈下降趋势，在Al欠量2％、4％和6％时，产物的纯度wfB）分别为95．08％、94．58％及94．15％。
英文摘要：
Boron powder was prepared by self-propagating aluminothermic reduction reaction using B2O3 and Al powders as raw materials and reductant, respectively. The effects of KClO3 addition content and the mass ratio of starting materials on the purity of products were systematically studied. The phases, morphology and elementary analysis of pure boron were characterized by XRD, SEM and EDS. The results show that the reductive products consist of ct-B and a small quantity of Al, B2O3, α-Al2O3 phases. The content of Boron in the products increases with the increasing of additive KClO3 content, whereas the content of A1 decreases. When the addition amount of KC103 is w（KCLO3）=25%, the content of Boron comes to maximum value of about w（B）=94.38% and the content of Al is w（A1）=5.62%. The purity of products decreases with the content of Al decreasing. When the contents （mass fraction, %） of Al are respectively deficiency of 2%, 4% and 6%, the purities of products are 95.08%, 94.58% and 94.15%, respectively.
同期刊论文项目
同项目期刊论文
White cast iron with a nano-eutectic microstructure and high tensile strength and considerable ducti
EFFECTS OF Al ELEMENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF HOT-ROLLED 316L STAINLESS STEEL
Investigation of Nanomechanical Properties of beta-Si3N4 Thin Layers in a Prismatic Plane under Tens
Effect of chromium content on microstructure and mechanical properties of large dimensional bulk nan
Theoretical Research of Electronic Structures and Optical Properties of beta-Si-2[Si(1-x)Ybx]N-4 (x=
Research of electronic structures and optical properties of Na- and Mg-doped b-Si 3 N 4 based on the
Effect of annealing on microstructure and mechanical properties of large dimensional bulk nanocrysta
Effect of Mn element on microstructure and mechanical properties of bulk nanocrystalline Fe3Al based
Effects of Different Substrates on Microstructures and Mechanical Properties of a Bimodal Bulk Nano/
Effect of substrates on microstructure and mechanical properties of nano-eutectic 1080 steel produce
Effect of annealing temperature on microstructure and mechanical properties of bulk 316L stainless s
Microstructure and tensile properties of 304 stainless steel with different combination of dual nano
Reduced graphene oxide-coated cottons for selective absorption of organic solvents and oils from wat
Microstructures and tensile properties of 304 steel with dual nanocrystalline and microcrystalline a
Insight into the nanomechanical properties under indentation of beta-Si3N4 nano-thin layers in the b
期刊信息
位置：