中文摘要：
以红土镍矿常压酸浸净化液为原料,采用阴离子交换膜与电解结合的方法制备金属镍。分别研究电解液成分、温度、时间、电流密度和p H等因素对阴极电流效率、回收率、能耗以及槽电压的影响。结果表明:含Ni2+溶液浓度为64 g/L、H3BO4浓度为40 g/L、H2SO4浓度为0.1 mol/L、温度为40℃、电流密度为300 A/m2、p H为5.2时,阴极电流效率达到98.47%,能耗为3470 k W·h/t,得到的金属镍纯度达到99.9%以上,能够满足工业上的要求。
英文摘要：
Ni was prepared by the method combining anionexchange membrane with electrolysis using nickel laterite atmospheric acid leaching purifying solution as main raw material. The influences of parameters including the electrolyte composition, temperature, time, current density, pH and other factors on the cathodic current efficiency, recovery rate, energy consumption and cell voltage were explored, respectively. The results indicate that the cathode current efficiency and the energy consumption are 98.47%, 3470 kW·h/t at Ni concentration of 64 g/L, H3BO4 concentration of 40 g/L, H2SO4 concentration of 0.1 mol/L, temperature of 40 ℃, pH of 5.2 and cathode current density of 300 A/m2, respectively,and the purity of this nickel can achieve more than 99.9%, which can meet the industrial requirements.
同期刊论文项目
同项目期刊论文
Preparation of Cr2O3 precursors by hydrothermal reduction in the abundant Na2CO3 and Na2CrO4 solutio
Activation pretreatment of low-grade Ti-slag by alkali roasting: Anticaking technique and kinetics o
Extraction of iron (III) from chloride leaching liquor with high acidity using tri-n-butyl phosphate
Pd nanoparticles supported on PDDA-functionalized Ti4O 7 as an effective catalyst for formic acid el
Removal of silicon in acid leaching and flocculation processes during zirconium oxychloride octahydr
Recovery of titanium from undissolved residue (tionite) in the titanium oxide industry via NaOH hydr
Electrocatalysis of carbon black- or poly(diallyldimethylammonium chloride)-functionalized activated
Preparation of activated carbon hollow fibers from ramie at low temperature for electric double-laye
Recovery of Ni, Co, Mn, and Mg from nickel laterite ores using alkaline oxidation and hydrochloric a
Mineralizer effects on the synthesis of amorphous chromium hydroxide and chromium oxide green pigmen
Dechromization and dealumination kinetics in process of Na2CO3-roasting pretreatment of laterite ore
Structural control of Na2TiO3 in pre-treating natural rutile ore by alkali roasting for TiO2 product
Study on Lithium Insertion in Lepidocrocite and lambda-MnO2 Type TiO2: A First-Principles Prediction
Controlling the formation of Na2ZrSiO5 in alkali fusion process for zirconium oxychloride production
A two-step zircon decomposition method to produce zirconium oxychloride: alkali fusion and water lea
Mechanism and kinetics of titanium hydrolysis in concentrated titanyl sulfate solution based on infr
Effect of ZnCl2 impregnation concentration on themicrostructure and electrical performance of ramie-
Innovative technology for processing saprolitic laterite ores by hydrochloric acid atmospheric press
Dechromization and dealumination kinetics in the process of Na2CO3-roasting pretreatment of laterite
期刊信息
位置：