中文摘要：
以微硅粉为硅源,CTAB和PEG-6000为模板剂,采用水热法制备得到MCM-41介孔分子筛.以该MCM-41为载体,采用后接技法将巯丙基三甲氧基硅烷引入到MCM-41的表面和孔道内,合成了巯基功能化的MCM-41介孔分子筛（SH-MCM-41）,并采用XRD、N2 吸附-脱附曲线和FT-IR对样品进行了表征.以巯基功能化的样品为吸附剂,对含Cr2O7＾2- 的溶液进行了静态吸附实验,研究了pH 值和初始浓度对吸附剂吸附性能的影响,探讨了吸附过程的热力学.结果表明,吸附剂吸附量随初始浓度和温度升高而增加,当pH 值为1时吸附容量最大,达25.5mg/g.不同温度下Langmuir方程均呈现很好的拟合度,热力学平衡方程计算得ΔG 〈0,ΔH =14.2kJ/mol,ΔS〉0,表明该吸附过程是自发的、吸热、熵增加的过程.
英文摘要：
Using the silica fume as silica source,CTAB and PEG-6000 as template agent,the MCM-41 meso-porous silica materials were successfully synthesized.3-Mercaptopropyl trimethoxysilane was introduced into the network of MCM-41 through post-grafting and thiol-functionalized MCM-41 mesoporous silica (SH-MCM-41)was obtained.The SH-MCM-41 was characterized by XRD,N2 adsorption-desorption isotherm,and FT-IR.Cr2 O2-7 adsorption characteristics in water solution have been studied in static experiments with the SH-MCM-41 as adsorbent.The influence of solution pH value and initial metal ion concentration was investigated. And the thermodynamics of Cr2 O2-7 adsorption onto SH-MCM-41 was also studied.It was showed that adsorp-tion capacity of Cr2 O2-7 increased with increasing initial metal ion concentration and temperature.And its high-est value was 25.5 mg/g at pH 1.Experimental data fitted well to the Langmuir model at all temperatures studied.The thermodynamic equilibrium functions were also determined.ΔG<0,ΔH=14.2 kJ/mol,ΔS>0, so the adsorption was spontaneous,endothermic and entropy increasing.
同期刊论文项目
同项目期刊论文
Effect of sodium-based slag treatment on the distribution of impurities in metallurgical grade silic
Precipitation phase and impurities distribution of MG-silicon by vacuum refining followed slag treat
Microstructural characterization in metallurgical grade silicon by slag treatment using CaO-SiO2 and
Evaporation and removal mechanism of phosphorus from the surface of silicon melt during electron bea
Effect of calcium-based slag treatment on hydrometallurgical purification of metallurgical-grade sil
Segregation and evaporation behaviors of aluminum and calcium in silicon during solidification proce
Determination and Controlling of Crystal Growth Rate during Silicon Purification by Directional Soli
he heat transfer effect on multicrystalline silicon crystal quality during vacuum directional solidi
Effects of Slag Refining on Boron Removal from Metallurgical- Grade Silicon Using Recycled Slag with
Effect of calcium-oxide on the removal of calcium during industrial directional solidification of up
Reaction Mechanism and Kinetics of Boron Removal from Metallurgical-Grade Silicon Based on Li2O-SiO2
Effects of Cu contamination on The Electrical Properties of Multicrystalline Silicon Purified by Dir
Distribution of representative impurities in MG-silicon using CaO-SiO2-CaF2 and CaO-SiO2-CaCl2 slags
Effect of Na2O-SiO2 slag treatment on hydrometallurgical purification of metallurgical grade silicon
Effect of withdrawal rate on defects of upgraded metallurgical grade (UMG)-silicon prepared by vacuu
期刊信息
位置：